Moulding Silicone Rubber for inner decoration

1.Advantage of moulding silicone  rubber:

moulding silicone  rubber is a kind of liquid  with good fluidity, fast curing speed, high tearing strength elongation, high tear strength.
 

2.Application of moulding silicone rubber :

silicone moulding rubber is mainly applicable to make the silicone mould for cultural relic duplication,architectural decoration, resin crafts, lighting ornaments, candles, statues, model design, product exploitation, etc. 

3.Features of moulding silicone  rubber :

RTV-2 moulding silicone rubber, silicon rubber are generally named two -component room temperature vulcanization silicone rubber, a kind elastic silicone rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion. 

4.Operation instructions of moulding silicone  rubber :

RTV-2 molding silicone rubber are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2-3% curing agent, they can still be operated within 30 minutes, but will be formed after 2-3 hours. With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli  crafts, resin crafts lighting and candle crafts. 

5.Frequently asked questions about moulding silicone  rubber.

What is RTV-2 moulding silicone rubber?

       The silicone mould making rubber (RTV-2) is a two-component room temperature vulcanization silicone rubber. Two parts of compounds have crosslinking reaction under the presence of catalyst to form a flexible elastomer.

     The silicone moulding rubber can be mainly used for various molds making, it is widely used in unsaturated resin, epoxy resin, polyurethanes decorations and crafts mold duplication and for furniture imitating ancient style, ceramics, artistic candle, artificial status, duplication of cultural relics, artificial imitation of natural stone, shoe mold, lighting arts, etc.

   silicone moulding rubber has good high temperature resistance, excellent tensile strength and tear strength, low shrinkage and not easy to deform, etc.

Keywords you inputted: RTV-2 moulding silicone rubber.

6.The proportions and reactions of the curing agent and the silicon are listed as

follows:

a. Adding curing agent 1%, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.

b. Adding curing agent 2%, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.

c. Adding curing agent 3%, the silicone can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.

d. Adding curing agent 4%, the silicone can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.