group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY630 silicone rubber
payment methodT/T, L/C, Westem Union
update timeTue, 05 Nov 2013 11:03:18 GMT
color white
certification RoHS, MSDS, SGS, ISO9001:2000
Min Order200 kilogram
RTV 2 silicone rubber for caved plaster sculpture
model of RTV 2 silicone rubber for caved plaster sculpture:
RTV 2 silicone rubber 630#
Model | 630# |
Appearance | white |
Mixing proportion of curing agent(%) | 5% |
Operating time ( hours ) | 0.5 |
Curing time( hours ) | 6 |
Hardness (A°) | 30 |
Density ( g/cm3) | 1.08 |
Viscosity (CS) | 23000 |
Tensile-strength ( kgf /cm2 ) | 40 |
Tear-strength (kgf /cm2 ) | 29 |
Elongation-break(%) | 520 |
Retractility(%) | ≤0.3 |
RTV 2 silicone rubber for caved plaster sculpture application:
PU resin, unsaturated resin, urethane resin, poly candles and gypsums crafts,toys,soap, statuary molds making,etc
TECHNICAL GUIDELINES ofRTV 2 silicone rubber for caved plaster sculpture molds making :
1. Added with 1 of curing agent, RTV 2 silicone rubber can still flow within 2.5 hours, mold can be released in 6-8 hours.
2. Added with 2 of curing agent, RTV 2 silicone rubber can still flow within 50 minutes to 1 hour, mold can be released in 23 hours.
3. Added with 3 of curing agent, RTV 2 silicone rubber can still flow within 2830 minutes, mold can be released in 1.52 hours.
4. Added with 4 of curing agent, RTV 2 silicone rubber can still flow wtithin 1015 minutes, mold can be released in 11.5 hours.
SHELF LIFE of RTV 2 silicone rubber for caved plaster sculpture molds making :
Twelve(12) months from date of shipment when stored at 24C in original unopened packages.
PACKAGE:
Packed in clean 25kg/pail, 200kg/pail.
Any questions of RTV 2 silicone rubber for caved plaster sculpture, please feel free to contact Ms orianna: