group nameRTV-2 silicone rubber for molds making
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelrtv 630#
payment methodT/T, L/C, Westem Union
update timeTue, 05 Nov 2013 12:10:06 GMT
color white
certifications RoHS
operation way brushing
hardness 30 shore A
shrinkage light shrinkage
visicosity light visicosity
deformation no deformation
elasticity good elasticity
duplication times high duplication times
Min Order100 kilogram
USERS INSTRUCTION
mold making silicone rubber for GFRC Columns are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability.When mixed with 4% 5% curing agent, they can still be operated within 50 minutes,but will be formed after 4-5 hours.With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.
TDS of mold making silicone rubber for GFRC Columns
Model:630#
Appearance:white/red
Viscosity(cs):15000-17000
Hardness(A):30
Tensile strength(kgf/cm)≥35-36
Elongation break(%):≥450
Retractility(%):≤0.3
Curing agent mixed rate(%):2-3
Operate time(min):30
Curing time(hours):2-4
Mixing proportion of curing agent:4%
Curing agent and silicon proportion and reaction(Under room-temperature-25C)
1,Added with 2% of curing agent, silicon can still flow within 1.2-1.5 hours, mold can be released in 7-8 hours.
2,Added with 3% of curing agent, silicon can still flow within 70mins to 1 hours, mold can be released in 6-7 hours.
3,Added with 4% of curing agent, silicon can still flow within 40-50 minutes, mold can be released in 5-6 hours.
TECHNICAL GUIDELINES
1. Stir the base (Part A) well beofre use (except when depending on machine ).
2. Shake the catalyst container (Part B) well before use.
3. This is a 100 Part A to 4 Part B mixing ratio by weight.Weigh the desire amount of base into a clean mixing container.
4. Weight the proper amount of catalyst into the container. Mix the base and catalyst together by stirring with a stick until a uniform color is obtained. Scrape the container walls and bottom well to insure a thorough mix.
5. Though it is often unnecessary to deair the material due to its low viscosity some may choose to do so. If so,place the container into a vacuum chamber and evacuate the entrapped air from the mixture using a vacuum pump capable of achieving 29 inches of mercury vacuum.The mixture will rise, crest and then collapse in the contanier. Interruption(bumping) of the vacuum may be necessary to prevent overflowing the container. Keep the mixture under full vacuum for 2-3 minutes.
6. Bleed air slowly into the vacuum chamber. When the chamber is at atmospheric equiplibrium,remove the cover plate and take out the container.
7. Pour the deaired material slowly in a steady stream from one end of the mould so that the material flows evenly over the pattern. This should minimize emtrapment of air bubbles under the flowing material. A”ready”mold may be poured firstly over the pattern, which will also help reduce the possibility of entrapping air on the pattern and in the cured rubber.A mold release agent may be applied on the pattern first to improve release.
8. Allow the rubber to cure for 2-4 hours at 24C before removing the cured rubber mold from the pattern. Heat acceleration not recommended with this product.
9. For best results, allow the mold to air cure an additional 24 hours before using it in production.
SHELF LIFE
Twelve(12) months from date of shipment when stored at 250C in the original sealed packages.
PACKAGE:
Packed in clean 25kg/pail, 200kg/pail.
Any questions of Silicone Rubber, please feel free to contact Miss Leah:
TEL: 086-755-89212382
FAX: 086-755-89948030
MOBILE: 086-189 3886 7561
Website: www(dot)szrl(dot)net
E-MAIL: hyji(at)szrl(dot)net
Skype: leahchou1214
QQ: 189 3886 7561
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.