Silicon rubber for plaster products

 Silicon rubber for plaster products 

Usage of Silicon rubber for plaster products:

Silicon rubber for plaster products is suitable for the mold making of large size products making in multiple pieces, reliefs, arts & crafts.

Description of Silicon rubber for plaster products:

Silicon rubber for plaster products is mainly used for toy gifts and craftwork gifts with the advantages of good tensile strength, high tear strength, high temperature resistance, high duplication times and repeated use, etc. It is suitable for small products or fine and precision products which is difficult to demould. This brushing silicon is one of the products with the highest use level in the production of craftwork gifts and the shrinkage is up to 2‰.

General Description of Silicon rubber for plaster products:

silicon rubber for plaster peoducts and brushing silicon are general called two-component room temperature vulcanization silicon rubber with excellent fluidity and good operational performance. Add curing agent of 2%-3% at the room temperature, the brushing silicon is still operational within 30 minutes,and in 2-5 hours, an elastic silicon mold will be obtained with resistance to deformation, high-temperature, acid and alkali and expansion. The brushing silicon is mainly applicable to mold duplication of poly crafts, resin craftworks, lightings, candles, etc. and fabrication of precision molds.

Operation Instruction for Silicon rubber for plaster products:

Silicon rubber for plaster products is white or red flowing liquid with general hardness of 23—27A°after curing . If the customer wants to make large products and large size molds, the mold should be made of silicon rubber with high hardness. On the contrary, if  the mold with fine and precision patterns , it should be made of silicon with low hardness. The amount of the curing agent depends on the actual requirements of the customer. If molds requiring fast drying and demould, more curing agent is needed; contrarily, if molds requiring slower drying and demould, less curing agent is needed.

(Note: our company does not recommend you to add silicone oil. If a special soft silicon mold or fine detailed and complex patterns products are required, 5%-10% silicon oil can be added to soften the mold for easy demould.)

The proportions and reactions of the Silicon rubber for plaster products is listed as follows:

1. Adding curing agent 1%, the silicon can still be operated within 2.5 hours and can be demoulded after 6-8 hours.

2. Adding curing agent 2%, the silicon can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.

3. Adding curing agent 3%, the silicon can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.

4. Adding curing agent 4%, the silicon can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.