group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY625# silicone rubber
payment methodT/T, L/C, Westem Union
update timeTue, 05 Nov 2013 13:06:30 GMT
Classification Chemical Auxiliary Agent
Other Names silicon rubber
Purity 99.9%
Type Other
Usage Coating Auxiliary Agents,Electronics Chemicals,Rubber Auxiliary Agents
color WHITE,RED,etc.
sample available
HS Code 39100000
Delievery Time Within 3 days after bank slip received
Trade Terms FOB/CIF/CNF/DDU
Payment terms T/T, L/C
MOQ 200kg
Hardness (A°) 25±2
Mixing Ratio of silicone and catalyst 100:3
Operating time (mins 25 0C ) 30-45
Min Order200 kilogram
1.Usages of shoe mould making silicones
shoe mould making silicones is primarily intended for candles crafts,candle mold,poly resin ,PU crafts, PU resin crafts ,gypsum crafts ,unsaturated resin crafts, lighting and plastic toy , printing irregular patterns of plastic toys, electroplating toys, trade makers , manual mold design, PVC plastic molds, cement product molds, melting point alloy molds, alloy toy craftworks, plastic toy craftworks, gifts and stationery, large statues, duplication of cultural relics.
2.Features of shoe mould making silicones:
shoe mould making siliconeswith features resistance to deformation, high-temperature, acid-alkali and expansion,abrasion ,solvent, aging and deformation resistance & good thermal conductivity with high print times & good printing effect, catalyst is free charged.,low shrinkage, good tensile strength & reproduction time on the need of customer.
3.Operations of shoe mould making silicones:
The proportions and reactions of the curing agent and the silicon are listed as follows:
1. Adding curing agent 1%, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.
2. Adding curing agent 2%, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
3. Adding curing agent 3%, the silicone can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.
4. Adding curing agent 4%, the silicone can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.
FAQ of shoe mould making silicones
Why could the silicone mold be reused only for a few times?
It can be due to the following reasons:
a. Adding too much silicone oil into silicon rubber. Silicon oil is an additive which destroies the molecular chain of silicone rubber and reduce the tension and tear strength.
b. Using the silicon rubber with a high hardness to make molds for small sized products with delicate and intricate designs and the silicon rubber with a low hardness to makes molds for large sized products with simple designs.
(Notes: we should choose the silicon rubber specifically according to the requirements of our products to avoid this problem.
If you have any questions withshoe mould making silicones, pls feel free to contact Ms Angel Yue
MSN: angelfly369(at)msn(dot)cn
Skype:angelfly369
Email:hysa(at)szrl(dot)net
Tel:0086-755-89948006
Mob: 086-18938867575
Trademanager:cn200039753
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.