group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHy 528#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 15:10:50 GMT
Application Mold making silicone rubber
H.S. code 39100000
Shelf life 12 months
Appearance Liquid
Curing agent / Catalyst 4% for free of charged
Mixing ratio 100:5 / 100:4/ 100:3
Sample Free
Package Vacuum packing
Certificate FDA,SGS, RoHS, MSDS, ISO9001:2000
Min Order200 kilogram
1.vantage of tire molding rtv silicone rubber:
car tyre mold making silicone rubber is a kind of liquid with good fluidity, fast curing speed, high tearing strength elongation, high tear strength
2.Application of tire molding rtv silicone rubber :
car tyre mold making silicone rubber is mainly applicable to make the silicone mould for cultural relic duplication,architectural decoration, resin crafts, lighting ornaments, candles, statues, model design, product exploitation, etc.
.
3.Features of tire molding rtv silicone rubber :
RTV-2 molding silicone rubber, silicon rubber are generally named two -component room temperature vulcanization silicone rubber, a kind elastic silicone rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion.
4.Operation instructions of tire molding rtv silicone rubber :
car tyre mold making silicone rubber are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2-3% curing agent, they can still be operated within 30 minutes, but will be formed after 2-3 hours. With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.
5.Datasheets of tire molding rtv silicone rubber :
Model | 528# |
Appearance | white |
Mixing proportion of curing agent (%) | 4-5% |
Operating time (mins 25 0 C ) | 30-60 |
Curing time(hours 25 0 C ) | 4 |
Hardness (A°) | 28-30 |
Density ( g/cm 3 ) | 1.08 |
Viscosity (mPas - 25 0 C ) | 28000-32000 |
Tensile-strength(kgf /cm 2 ) | 4.0-4.4 |
Tear-strength (kgf /cm ) | 22-26 |
Elongation-break( % ) | 360-400 |
Retractility( % ) | ≤0.3 |
6.requently asked questions about mold making silicone.
What is mold making silicone?
1)e mold making silicone (RTV-2) is a two-component room temperature vulcanization silicone rubber. Two parts of compounds have crosslinking reaction under the presence of catalyst to form a flexible elastomer.
2)e mold making silicone can be mainly used for various molds making, it is widely used in unsaturated resin, epoxy resin, polyurethanes decorations and crafts mold duplication and for furniture imitating ancient style, ceramics, artistic candle, artificial status, duplication of cultural relics, artificial imitation of natural stone, shoe mold, lighting arts, etc.
3)ld making silicone has good high temperature resistance, excellent tensile strength and tear strength, low shrinkage and not easy to deform, etc.
7.The proportions and reactions of the curing agent and the silicon are listed as followers
a Adding curing agent 1%, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.
b Adding curing agent 2%, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
c Adding curing agent 3%, the silicone can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.
d Adding curing agent 4%, the silicone can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.
.
Any question abt tire molding rtv silicone rubber please feel free to ask Cindy
Tel :86-1893886 7554
Emial:hysg(at)szrl.net
Skype:cindyyeah5
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.