group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelrtv 630#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 16:10:38 GMT
color white
certifications RoHS
operation way brushing
hardness 30 shore A
shrinkage light shrinkage
visicosity medinum visicosity
deformation no deformation
elasticity good elasticity
duplication times high duplication times
Min Order200 kilogram
USES of Silicone Rubber for Plaster Molds Making
CRAFTS: poly resin crafts, PU resin crafts, gypsum crafts, unsaturated resin crafts, lighting and candles crafts, stationery gifts crafts
OTHER MATERIALS MOLD: a large statue Buddha, relievo furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, large-scale cement mold, artificial fossils Factory, Europe component factory, simulation landscapes, animals and plants sculpture, sandstone crafts and so on.
FEATURES of Silicone Rubber for Plaster Decoration Molds Making
Good cut-growth resistance
High durometer hardness
Low shrinkage
Easy release
Room temperature cure within 24 hours
Heat-accelerable cure
Long mold life
Highly detailed reproductions
Simplified handling
TDS of Silicone Mold Making Rubber for Decorative Plaster Molds
Model | 630 | GI-384GI-384 of Silicone, INC. |
Color | White | White |
Mixing ratio | 2~3% | 5% |
Pot life (mins, 25°C) | 30~50 | 60~120 |
Curing time (hrs, 25°C) | 4-5 | 16~18 |
Hardness ( shore A ) | 30±2 | 25~30 |
Tensile-strength (psi ) | 1000± 25 | 450 ± 25 |
Tear-strength (ppi) | 140± 25 | 125 ± 25 |
Viscosity(cps) | 27000 ± 3000 | 10,000-20,000 |
Shelf life (25°C) | 10~12months | 6 months |
TECHNICAL GUIDELINES OF Silicone Mold Making Rubber for Decorative Plaster Molds
1. Stir the base (Part A) well beofre use (except when depending on machine ).
2. Shake the catalyst container (Part B) well before use.
3. This is a 100 Part A to 4 Part B mixing ratio by weight.Weigh the desire amount of base into a clean mixing container.
4. Weight the proper amount of catalyst into the container. Mix the base and catalyst together by stirring with a stick until a uniform color is obtained. Scrape the container walls and bottom well to insure a thorough mix.
5. Though it is often unnecessary to deair the material due to its low viscosity some may choose to do so. If so,place the container into a vacuum chamber and evacuate the entrapped air from the mixture using a vacuum pump capable of achieving 29 inches of mercury vacuum.The mixture will rise, crest and then collapse in the contanier. Interruption(bumping) of the vacuum may be necessary to prevent overflowing the container. Keep the mixture under full vacuum for 2-3 minutes.
6. Bleed air slowly into the vacuum chamber. When the chamber is at atmospheric equiplibrium,remove the cover plate and take out the container.
7. Pour the deaired material slowly in a steady stream from one end of the mould so that the material flows evenly over the pattern. This should minimize emtrapment of air bubbles under the flowing material. A”ready”mold may be poured firstly over the pattern, which will also help reduce the possibility of entrapping air on the pattern and in the cured rubber.A mold release agent may be applied on the pattern first to improve release.
8. Allow the rubber to cure for 2-4 hours at 24C before removing the cured rubber mold from the pattern. Heat acceleration not recommended with this product.
9. For best results, allow the mold to air cure an additional 24 hours before using it in production.
SHELF LIFE OF moldmaking silicone rubber for GRC decor
Twelve(12) months from date of shipment when stored at 250C in the original sealed packages.
PACKAGE:
Packed in clean 25kg/pail, 200kg/pail.
Any questions about Silicone Rubber, Leah is at your service.
TEL: 086-755-89212382
FAX: 086-755-89948030
MOBILE: 086-189 3886 7561
Website: www(dot)szrl(dot)net
E-MAIL: hyji(at)szrl(dot)net
Skype: leahchou1214
QQ: 189 3886 7561
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.