200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE-642# silicone rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 16:51:38 GMT
Shrinkage rate <0.3
Color White
Mixing ratio 100:3
Pot life 30-40 mins
Curing time 4-6 hous
Package 25 kg/drum and 200 kg/drum
Shelf life 12 months
Delivery time 3-5 days after payment confirmed
HS. Code 39100000
Certificate Rohs, ISO 9001:2000
Min Order200 kilogram
Platinum Based Silicones For Jewelry Casting Description :
Platinum Based Silicones For Jewelry Casting are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.
Platinum Based Silicones For Jewelry Casting Main application:
Platinum Based Silicones For Jewelry Casting Main properties:
Platinum Based Silicones For Jewelry Casting
(The mixing ratio of part A and part B can be adjusted to 1:1or 10:1)
Product | E-615 | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 15±2 | 20±2 | 25±2 | 30±2 | 42±2 |
Mix ratio(A:B) | 1:1 | 1:1 | 1:1 | 1:1 | 10:1 |
Viscocity Part A(mPa.s) | 22000±2000 | 23000±2000 | 27000±2000 | 25000±2000 | 55000±2000 |
Viscocity Part B(mPa.s) | 1900±500 | 1900±500 | 1800±500 | 2400±500 | 150±50 |
Tensile strength (MPa) | 5.2 | 5.7 | 6.7 | 5.5 | 7.6 |
Tear-strength (kN/m) | 25 | 26 | 23 | 24 | 22 |
Elongation(%) | 569 | 581 | 480 | 410 | 450 |
Density | 1.05 | 1.05 | 1.07 | 1.13 | 1.14 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 20-30mins(60°C) | 6-8hrs(25°C) 130-50mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
Notice:
All above addition silicone is forbidden to mix with organic compounds of condensation cure silicone rubber,otherwise, the silicone rubber will not cure, and also should not mix with organic compounds containing S, P, N as well as metallic salt of organic acids. It also will cause this product cure uncompletely or not cure.
Any more information required of Platinum Based Silicones For Jewelry Casting, please feel free to contact Ms. Judy
MOBILE:086-18938867591
QQ:18938867591
SKYPE: judy.zhao723
Website: www(dot)szrl(dot)net
E-MAIL: hyja(at)szrl(dot)net