group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE625#silicone rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 17:31:48 GMT
Appearance Translucent
Hardness(shore A) 25±2
Mix ratio(A:B) 1:1/10:1
Viscocity Part A (mPa.s) 27000±2000
Viscocity Part B (mPa.s) 3500±500
Tensile strength (kgf/cm2) 48±5
Tear-strength (kN/m) 22±2
Elongation(%) 500±50
Pot life/working time (mins) 30-40
Curing time/setting time (hrs) 3-4hrs(25℃)10-20mins(60℃)
Min Order200 kilogram
1.Applications of Platinum Cure Silicone Rubber For Silicone Mold Making :
silicones for poly-addtion curing is primarily intended for food grade products moldmaking, such as baby nipples, chocolates molds, cake molds, ect.
It can also be used for plaster casting, resin casting, polyester casting, wax casting, gypsum casting, cement mold casting, silicone soap mold making, silicone candle mold making as well as low-melting point alloy crafts casting.
2.Features and Properties of Platinum Cure Silicone Rubber For Silicone Mold Making
1.Platinum Cure Silicone Rubber for Mold making
2.3.1:1 simple mix
3.Low shrinkage
4.With FDA certificate,specially for chocolate mold, faux food mold, silicone fuit mold making.
3. Introduction/Description of Platinum Cure Silicone Rubber For Silicone Mold Making :
Platinum Cure Silicone Rubber For Silicone Mold Making is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation and low shrinkage.
Model | HY-E625# |
Appearance | Translucent |
Mixing Ratio | 1:1 |
Operating time (Mins 25°C) | 30 - 50 |
Curing time (Mins 25°C) | 120 - 240 |
Curing time (Mins 60°C) | 20 - 30 |
Hardness (A°) | 25±2 |
Density ( g/cm 3 ) | 1.08 |
Viscosity (CS) (Part A) | 30000 ± 5000 |
Viscosity (CS) (Part B) | 5000 ± 500 |
Viscosity (CS) (After mixed) | 10000 ± 2000 |
Tensile-strength( kgf /cm2 ) | 55± 5 |
Tear-strength (kgf /cm2 ) | 15 ± 2 |
Elongation-break(%) | 500 ± 50 |
Retractility(%) | ≤0.1 |
4.Why does the silicone rubber mold have few molding times?
The silicone rubber mold has few molding times is due to follwoing reasons: adding too much silicone oil which will destroy the molecular of silicone rubber; making the mold for small and fine detailed products with higher hardness silicone rubber which is easy to break; making the mold for large products with soft silicone rubber which will reduce the tensile and tear strength of the mold, and the mold will have deformation. Thus, we should take the proper silicone rubber to make the mold for suitable products.
Minimum Order Quantity: 200 Kilogram
Packaging Details: 25kg/drum and 200kg/drum
Delivery Time: within 3 days after payment confirmed in our bank.
If you have any questions with Platinum Cure Silicone Rubber For Silicone Mold Making , pls feel free to contact Ms Angel Yue
MSN: angelfly369(at)msn(dot)cn
Skype:angelfly369
Email:hysa(at)szrl(dot)net
Tel:0086-755-89948006
Mob: 086-18938867575
Trademanager:cn200039753
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.