Low shrinkage tire molding silicone

FOB Price

US $20.00
100 - 40,000 kilogram
US $11.00
40,001 - 999,999 kilogram

group nameAddition cure silicone rubber
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelHY-620
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 18:16:24 GMT

contact supplier

Paramtents

color white/ off-white/ blue/ red
HS. Code 39100000
Purity 100%
Appearance Liquid
Application Mold Making Silicone Rubber
Sample Free
Catalyst 4% free of charged
MOQ 100KGS
Molding method Pouring , brushing
Certification SGS, RoHS, MSDS, FDA, REARCH, ISO9001:2000

Packging & Delivery

Min Order100 kilogram

Briefing

Low shrinkage tire molding silicone is kind of silicone rubber which is specialize for tyre molding, tyre casting, tyre mould.

Detailed

Low shrinkage tire molding silicone

Low shrinkage tire molding silicone Description

Low shrinkage tire molding silicone is generally named two-components silicone rubber, Part A and part B. It features an exceptional fluidity and good operability. The mixing ratio is 1:1 (10:1),mainly be suitable for making molds application.

Low shrinkage tire molding silicone Typical Applications

Low shrinkage tire molding silicone could be mainly used for making concrete stones, wax molds, PU molds, resin molds, gypsum casting, candle molding and chocolate , candy and any other FDA food product mold making,prototyping etc.

Low shrinkage tire molding silicone is has been used for years to make tire pattern molds .

Low shrinkage tire molding silicone Characteristics

*low shrinkage (less than 0.1% )

*high tensile and tear strength with high copy times

*easy for operation (mixing ratio at 1:1 /10:1)

*very good flow and easy for pouring operation

*Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat

Low shrinkage tire molding silicone

Low shrinkage tire molding silicone Technical Parameters

Product	E-620
Appearance	Translucent
Hardness(shore A)	20±2
Mix ratio(A:B)	1:1/10:1
Viscocity Part A(mPa.s)	23000±2000
Viscocity Part B(mPa.s)	3500±500
Tensile strength (kgf/cm2)	45±5
Tear-strength (kN/m)	20±2
Elongation(%)	500±50
Pot life/working time (mins)	30-40
Curing time/setting time (hrs)	3-4hrs(25°C) 110-20mins(60°C)
Shrinkage rate (%)	0.1

(Please note: the above data for this product in 25°C temperature, 55percent humidity conditions, for reference. The accurate data is measured by customers when using.)