group nameelectronic potting silicone rubber
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelHY160#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:28:48 GMT
Color Gray
Certificate UL94-V0
Package Vacuum Pumping
Shelf Life 12 months
Application For industrial controls, transformers, amplifiers
MOQ 200 kg
shape liquid
delivery within 3 days after payment
payment terms T/T, L/C
Min Order100 kilogram
RTV-2 Silicone HY160
Typical Application ofRTV-2 Silicone HY160
HY 160 is mainly used for general sealing for power supplies, connectors, sensors, industrial controls, transformers, amplifiers, high voltage resistors, relays and so on , It is provide as Two part seperated packing, mix part A and part B at the mix ration of 1:1 by weight.
Product Feature of RTV-2 Silicone HY160
l Room temperature vulcanization, and easy to operate;
l Mix Ration : 1 : 1 by weight
l Moderatethermal conductivity
l Firproof of ULV-0
Technical Parameters of RTV-2 Silicone HY160
Before Curing | Appearence | A : Black fluid , B white fluid |
Density(25°C g/ml) | 0.98±0.02 | |
Viscosisty(25°Ccps) | Part A 8000; Part B:4000 | |
Mixing Ratio | A:B=1:1(By weight) | |
Operating Time(25°C min) | 90 | |
Curing time(25°C Hour) | 6-8 | |
specific gravity | 1.57 | |
Shelf life (25°C , month) | 18 | |
After Curing | Hardness(Shore A) | 50-60 |
Dielectric Strength(KV/mm) | 19 | |
Volume Resistance(Ω.Cm) | 1.0×1016 | |
Permittivity(100Hz) | 3.51 | |
Temperature Resistence(°C) | -60~200 | |
Fire Resistance | UL94-V0 | |
linear expansibility[m/(m·K)] | 2.2×10-4 |
(Pls note: the above data for this product based on 25 °C temperature, 55 % humidity for reference. We will not be responsible for test difference of product propetise if customer adjust custom by themsel or not test in standard labory condition.)
TECHNICAL GUIDELINES of RTV-2 Silicone HY160
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Weight Ratio: part A: part B = 1:1
3, Deaeration the mixture under 0.08 MPa for 5 minutes.
4, The temperature influences the curing time of HY160. When in too low temperature, the operation time will be longer, Under the room temperature , curing time will be 10-12hours.
Warm Tips:
1.The following material may hinder the curing of the product,:
Condensation silicone which not completely cured or organic tin compounds
l Sulphur, sulfide and sulfur rubber materials.
l Amine compounds as well as contains the amine materials.
l Pewters solder flux.
2. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.
3. When it gets stratified after a period of storage, Please mix 160 evenly before using, it does not affect the performance.
PACKAGE of RTV-2 Silicone HY160
20kg or 200kgs per drum . the same package of the part A and B .
SHELF LIFE AND TRANSPORTATION
1. Eighteen (18) months from date of shipment when stored at 25C in original unopened packages.
2. This kind of product is non-dangerous product, it can be transported as general chemicals.
3. Products exceed the storage life should be confirmed normal before using.
For more information, pls contact with Miss Caroline at any time!
Tel: +86-755-89948019
Mobile: +86-18938867567
Skype: cathy19900719
Email: hysf(at)szrl(dot)net
Website : www(dot)szrl(dot)net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.