group nameelectronic potting silicone rubber
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelHY-9055 HY-9500
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:39:56 GMT
Type Charm,Coin,Digital,Fashion,Limited Edition,Luxury,Quartz,Sport,LED
Feature Alarm,Auto Date,Chronograph,Complete Calendar,Day/Date,Diver,Heart Rate Monitor,Not Specified,Perpetual Calendar,Power Reserve,Rattrapante,Repeater,Water Resistant
Material Silicone,liquid silicone with two part
Gender Not Specified
Age 1998
payment TT /LC /West union
certificates Rohs,Msds,Sgs,ISO9001:2000
color white red,green or as your need
features white ,good tension,low viscosity, suitable hardness
mix 1:1 or 10:1
promotion over 500KG 2% discount
environmental protection yes
samples available
usage LED Electronic Potting
Min Order100 kilogram
Electronic Potting Silicone Rubber for LED
Typical Application
Electronic Potting Silicone Rubber for LED is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
Product Feature
It can be applied to the sealing and pouring of various electronic components, and then forming insulation system with no corrosion and negligible shrinkage.
l Room temperature vulcanize, and easy to operate;
l Maintain flexibility at a wide temperature range, and excellent insulation performance;
l Waterproof, moisture-proof, mouldproof, dustproof, and stable components;
l Resistance to Chemical dielectric, anti-yellowing, resistance to climate ageing.
Technical Parameters
Before Curing | Appearence | Black Fluid |
Density(25°C g/ml) | 0.98±0.02 | |
Viscosisty(25°Ccps) | Part A 2500±500;Part B:2500±500 | |
Mixing Ratio | A:B=1:1(By weight) | |
Operating Time(25°C min) | 120 | |
Curing time(25°C min) | 480 | |
Curing time(80°C min) | 20 | |
After Curing | Hardness(Shore A) | 50-60 |
Dielectric Strength(KV/mm) | 23 | |
Volume Resistance(Ω.Cm) | 1.0×10 15 | |
Permittivity(1.2MHz) | 3.0 | |
Temperature Resistence(°C) | -60~200 | |
Fire Resistance | UL94-V1 | |
| Arc Resistance | 250V |
|
|
|
(Pls note: the above data for this product in 25 °C temperature, 55 percent humidity conditions, for reference. The accurate data is measured by customers to when using.
The appearance can be adjusted by our technical department if required.)
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Weight Ratio: part A: part B = 1:1
3, Deaeration the mixture under 0.08 MPa for 3 minutes.
4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.
Warm Tips:
1.The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.
l Condensation silicone which not completely cured or organic tin compounds
l Sulphur, sulfide and sulfur rubber materials.
l Amine compounds as well as contains the amine materials.
l Pewters solder flux.
2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.
3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix 9301 evenly before using, it does not affect the performance.
PACKAGE
20Kg/pail (Part A10Kg + Part B10Kg)
SHELF LIFE AND TRANSPORTATION
1. Twelve(12) months from date of shipment when stored at 24C in original unopened packages.
2. This kind of product is non-dangerous product, it can be transported as general chemicals.
3. Products exceed the storage life should be confirmed normal before using.
For more information, please feel free to contact with Mr Wenson:
TEL: 0086-755-89948019
FAX: 0086-755-89948030
MOBILE: 0086-18938867531
skype: wensona
E-mail:hyb(at)szrl(dot)net
website:www(dot)szrl(dot)net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.