200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE630
payment methodT/T, L/C, Westem Union
update timeSat, 09 Nov 2013 12:24:59 GMT
Sample Free
Shelf Life 18 months
Certificate ISO9001:2000,FDA,RoHS
Operating time (hour 25 0C ) 0.5
Colour Any
Hardness(shore A) 15-42
Mix Ratio 1;1
Elongation-break(%) 320-520
Curing time(hour) 3-5
Dynamic Viscosity (mPa.s) 8000-14000
Min Order200 kilogram
Platinum cure silicone rubber for chocolates moldes
1.Description of Platinum cure silicone rubber for chocolates moldes
Platinum cure Silicone Rubber For chocolates moldes are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.
2.Applications of Platinum cure silicone rubber for chocolates moldes
Especially suitable for the molding
for food moulding like chocolates, cake etc
for plaster decoration duplication,
for gypsum sculpture reproduction,
for duplicating resin product with fine details,
for PU resin reproduction,
for wax molding,
for stone duplication ,
for reproducing polyester craft
3.Features of Platinum cure silicone rubber for chocolates moldes
/Good fluidity and good operability and good for pouring method.
/Excellent mechanical properties, in particular tear strength and tensile strength.
/Excellent flexibility and it is easy to demould.
/High temperature resistance, high duplication times and repeated use.
/There are a range of catalysts/curing agent/hardener allows the Liquid rtv silicone rubber to fulfill requirements for various applications and various requirements on the operation time and curing time.
4.Operation ways of Platinum cure silicone rubber for chocolates moldes
1.The cast pouring, for example:
Prepare a frame, fix the prototype for copy into the frame, (if the prototype’s material is glass or ceramic, the release agent is necessary to prevent sticking.
2. Take 1 part A and 1 part B,mix themevenly.
3.Vacuum defoaming in 1~3 min,inject the rubber into the type box, then vacuum defoaming again, curing 24 hours in nature room temperature, use it after demold.
4. Demold after 3 hours’ room temperature curing, and then use it after 24 hours’ keep mold under the same condition.
5.Datasheet of Platinum cure silicone rubber for chocolates moldes
Model | E-615 | E-620 | E-625 | E-630 |
Appearance | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 15±2 | 20±2 | 25±2 | 30±2 |
Mix ratio(A:B) | 1:1 | 1:1 | 1:1 | 1:1 or 10:1 |
Viscocity (mPa.s) | 8000±2000 | 9000±2000 | 10000±2000 | 12000±2000 |
Tensile strength (MPa) | 4.7 | 5.2 | 5.8 | 5.8 |
Tear-strength (kN/m) | 14±2 | 16±2 | 15±2 | 14±2 |
Elongation(%) | 500 | 550 | 500 | 500 |
Density | 1.05 | 1.05 | 1.07 | 1.13 |
Pot life/working time (mins) | 20-40 | 20-40 | 20-40 | 20-40 |
Curing time/setting time | 3-5hrs(25°C) | 3-5hrs(25°C) | 3-5hrs(25°C) | 3-5hrs(25°C) |
20-30mins(60°C) | 20-30mins(60°C) | 20-30mins(60°C) | 20-30mins(60°C) | |
Shrinkage rate (%) | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 |
6.Package of Platinum cure silicone rubber for chocolates moldes
7.Certificationsof Food grade addition cure silicone rubber for chocolates moldes
8.Our factory:
Need the price or other information for reference,please help us confirm some question first
1) How about the size of your products?
2) Will you make the silicone mold by pouring way or brushing way ?
3) What's the raw material of your products ? Plaster? resin or other?
Then we will according it to recommend the most suitable RTV silicone with the best price for your reference.
Any questions, please feel free to contact Mr Lucas:
TEL: 086-755-89212369
FAX: 086-755-89948030
MOBILE:086-18898736056
E-mail: hysj(at)szrl(dot)net
You can also send me E-mail by scanning QR Code below:
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.