Shoe sole liquid silicon

FOB Price

US $5.50
200 - 40,000 kilogram
US $4.60
40,001 - 999,999 kilogram

group nameLiquid silicone rubber for insoles
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-540 silicone
payment methodT/T, L/C, Westem Union
update timeSat, 09 Nov 2013 12:46:53 GMT

contact supplier

Paramtents

color red/white/yellow/green
Certifications RoHS.MSDS.SGS

Packging & Delivery

Min Order200 kilogram

Briefing

Light viscosity and good flowability;
Low shrinkage;
Favorable tension;
No deformation;
High temperature resistance.

Detailed

Shoe sole liquid silicone

Shoe sole liquid silicone Usage:

For the duplication of manual mold, low melting point alloy mold,toy crafts.

Standard Datasheet of Shoe sole liquid silicone:

Model	Appearance	Viscosity (cps)	Hardness (Ao)	Tensile Strength (Mpa)	Tear Strength (KN/m)	Elongation (%)	Mixing Ratio(%)	Pot life (H)	Demould time(H)
540	White	≤18000	38±2	≥2.0	≥7	≥200	2~3	0.5	2~4

Shoe sole liquid silicone Description:

Shoe sole liquid silicone is flowing liquid with consistant quality in whatever color. It consists of two components, wherein component A is silicone rubber, and component B is curing agent or vulcanizing agent. Firstly process and prepare the model mold or the product to be duplicated, take certain amount of the silicone rubber, add 2- 3% solidifying agent, and mix evenly for use. One mold pair can be solidified and formed in 2-3 hours. The formed mold can be used repeatedly without deformation and water shrinkage and with high temperature resistance, thereby providing fast duplication of the product with a product shrinkage 2‰. The 528 manual mold silicon is mainly applicable to manual molds and small number of product duplication

Frequently asked questions for RTV silicone rubber, liquid silicone rubebr for shoe mold

What should we do when the air bubbles appeared in the process of mold making ?

To handle this situation depends on different cases. Under the condition of an available vacuum pumping machine, mix the silicon rubber and curing agent evenly and then take it to vacuum chamber to deair . If without a vacuum pumping machine, reduce the amount of the curing agent properly. For example, change the mixing ratio of the silicon rubber and the curing agent from former 4% to 1%-2%. In this way, the pre- crosslinking time of silicon rubber will slow down, so the air in the mold will be eliminated gradually to reduce the air bubbles.

For get further information about our silicone product, PLS contact with Miss Rose

Mobile:086-18938867525

TEL: 0086-75589948013

FAX: 086-755-89948030