JIS G3460 Steel Pipes for low temperature service

  • group nameBoiler Tubes

  • Min Order1 piece

  • brand namefushun

  • modelJIS G3460

  • payment methodT/T, L/C, D/P D/A

  • update timeThu, 19 May 2022 15:17:16 GMT

Paramtents

  • Type Hot Rolled / Cold Drawn

  • Delivery Condition As Rolled, Cold Drawn, Normalizing Rolled

Packging & Delivery

  • Min Order1 piece

Briefing

JIS G3460 Steel pipes used for piping at extremely low temperatures of freezing point or under

Detailed

JIS G3460 Steel pipes for low temperature service

 

JIS G3460 Steel pipes used for piping at extremely low temperatures of freezing point or under

 

JIS G3460 Steel pipes Manufacturing method

The manufacturing method shall be as follows.

The pipes shall be manufactured from fine-grained killed steels. Pipes of STPL380 shall be seamless or electric resistance welded, and those of STPL450 and STPL690 shall be seamless.

 

JIS G3460 Steel pipes dimensional and tolerances

Outside diameter: 10.5-660.4mm

wall thickness: sch 10-160

dimensional and tolerances: +/-1% OD ; +/- 1.6mm WT

 

JIS G3460 Steel pipes Chemical composition

Symbol of grade

C

Si

Mn

P

S

Ni

STPL380

0.25 max.

0.35 max.

1.35 max.

0.035 max.

0.035 max.

/

STPL450

0.18 max.

0.10 to 0.35

0.30 to 0.60

0.030 max.

0.030 max.

3.20 to 3.80

STPL690

0.13 max.

0.10 to 0.35

0.90 max.

0.030 max.

0.030 max.

8.50 to 9.50

 

JIS G3460 Steel pipes Mechanical properties

Symbol of grade

Tensile strength

N/mm2

Yield point or

proof stress N/mm2

Elongation %

Tensile test piece and tensile test direction

Test piece No.

11 or No. 12

Test piece

No. 5

Test piece No. 4

Parallel to pipe axis

Perpendicular to pipe axis

Parallel to pipe axis

Perpendicular to pipe axis

STPL380

380 min.

205 min.

35 min.

25 min.

30 min.

22 min.

STPL450

450 min.

245 min.

30 min.

20 min.

24 min.

16 min.

STPL690

690 min.

520 min.

21 min.

15 min.

16 min.

10 min.

 

JIS G3460 Steel pipes Heat treatment

STPL380/STPL450 Normalizing, normalizing followed by tem pering, or quenching followed by tempering

STPL690 Normalizing twice followed by tempering, or quenching followed by tempering

 

JIS G3460 Steel pipes Appearance

Appearance shall be as follows.

a) The pipes shall be straight, and the both ends shall be perpendicular to the pipe axis for practical purposes.

b) Both the internal and external surfaces of pipes shall be smoothly finished and free from defects detrimental to use.

c) Pipes may be repaired by grinding or machining, provided that the wall thickness of the product after repairing satisfies the specified tolerances. Repair by weldingis not permitted.

d) The surface of the repaired part shall be smooth along the contour of the pipe.

e) The external surface of the part where a weld bead was removed shall be smooth along the contour of the pipe.

 

JIS G3460 Steel pipes Tests and Inspection

Chemical analysis

Mechanical tests

Tensile test

Flattening test

Bend test

Charpy impact test

Hydrostatic test

Non-destructive test

 

Nearest port for product export
Tianjin, Qingdao, Shanghai, Huangshi
Delivery clauses under the trade mode
FOB, CFR, CIF, CIP, CPT, DDP, DDU, DAF
Acceptable payment methods
T/T, L/C, D/P D/A
Contact Suppliers

Follow this Suppliers