200 - 2,000 kilogram
group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelliquid silicone rubber for HY528
payment methodL/C, T/T, Western Union, cash,paypal
update timeWed, 23 Mar 2016 11:26:36 GMT
color white and trasparent
samples available
brand hong ye silicone rubber
HS 31900000
application shoe mold making
origin China
mixing ratio 3%
certificates FDA,SGS,
tear strength 28 Kn/M
delivery after 5 days
Weight1.25kg / kilogram
Min Order200 kilogram
shoe soles silicone rubber mainly used for shoe molds, sand casting, sole sampling, plaster models, simple products, products with non-complex patterns, as well as product models with stable size and non-deformation.
Standard Datasheet of shoe soles silicone rubber
Model: 218#
Appearance :white
Viscosity (cps) :15000
Hardness (A):18
Tensile Strength (kn/m) ≥5
Tear Strength (Mpa) ≥1.3
Elongation (%)≥300
Mixing ratio (%):2~3
Operating Time(h)0.5
Curing Time(h): 2~4
Using Instruction of shoe soles silicone rubber: Component A is white flowing liquid and component B is the curing agent. For example, take silicone rubber of 100g and add 2% curing agent for mixing evenly. After the silicone rubber and the curing agent are completely mixed, put the silicon into a vacuum machine for deairing to remove the bubbles. After deaired, pouring the liquid silicone rubber into the product to be duplicated or into the mold frame.
Note of shoe soles silicone rubber: silicone rubber for shoe sole mold making is used for pouring or brushing technique. That is to say, fix the product or sole model to be duplicated onto a plane plate, then enclose the plane frame with wooden plates to prevent the leakage of the silicon, mix the silicone rubber and the curing agent evenly according to the mixing ratio of 100: 2 and pour them onto the sole model, then brush evenly with a wooden plate or a brush, and fill up the mold frame with gypsum after the silicone rubber is dried.
Any more details,welcome to contact Ms.Raemon for more information:
Name:Raemon Shi
Email:raemon(at)szrl.net
Tel:0086-18948315840
Skype:wendy.wen121
Wechat:18948315840
FaceBook: https://..........com/RaemonShi
Website:..........net
Company:ShenZhen HongYeJie Technology Co.,Ltd.
Modle | Mix Ratio | Mix viscosity | pot life ( mins) | Cure time( hours at 25C) | Hardness | Shrinkage | Tensile Strength (MPa) | Tear-Strength((kN/m)) | Elongation at Break (%) | Color |
HYE610# | 1:1 or 10:1 | 1500±2000 | 20-40 | 3-5 | 10±2 | 0.001 | 3.2 | 12±2 | 600-700 | Translucent |
HYE615# | 1:1 | 6000±1000 | 20-40 | 3-5 | 15±2 | 0.001 | 4.2 | 12±2 | 470 | Translucent |
HYE620# | 1:1 | 7000±2000 | 20-40 | 3-5 | 20±2 | 0.001 | 4.7 | 25±2 | 520 | Translucent |
HYE625# | 1:1 | 8000±2000 | 20-40 | 3-5 | 25±2 | 0.001 | 5.2 | 25±2 | 470 | Translucent |
HYE630# | 1:1 | 9000±2000 | 20-40 | 3-5 | 30±2 | 0.001 | 5.2 | 20±2 | 470 | Translucent |
HYE640# | 1:1 | 20000±2000 | 10-40 | 6-8 | 40±2 | 0.001 | 5.6 | 22±2 | 400-500 | Translucent |
HYE650# | 1:1 | 10000±2000 | 20-40 | 3-5 | 50±2 | 0.001 | 5.3 | 12±2 | 300 | Translucent |
HYT640# | 1:1 | 40000±2000 | 10-60 | cured by heating 30mins at 120℃ | 40±2 | 0.001 | 5-6 | 20±2 | 400-500 | transparent |
Q630 | 1:1 | 16000±2000 | 20-40mins | 3-5H at 25℃ 20-30mins at 60℃ | 30±2 | 0.1% | 3.3 | 8±2 | 420 | transparent |