Electronic Potting Compound silicone rubber

FOB Price

US $12.88
200 - 1,000 kilogram

group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-9055# silicone rubber
payment methodL/C, T/T
update timeTue, 25 Mar 2014 15:32:24 GMT

contact supplier

Paramtents

Color white
sample free
application molding silicone
appearance liquid silicon
Place of Origin Guangdong, China (Mainland)
MOQ 200kg
Payment T/T L/C Western union
Package 25kg/drum 200kg/drum
Port shenzhen
Certifications RoHS, MSDS, SGS, ISO9001:2000

Packging & Delivery

Min Order200 kilogram

Briefing

RTV silicone suitabe for small size artcrafts mold making, such as resin toyes, little size sculptures..features good elastic..

Detailed

Product Feature
RTV-2 Silicone is a newly insulating material silicon of silicon compounds.
It cures without heat, corrosion and just with little shrinkage. It can be applied to the sealing and pouring of various electronic components, and then forming insulation system.
Features:

lRoom temperature vulcanize, and easy to operate;

lMaintain flexibility at a wide temperature range, and excellent insulation performance;

lWaterproofing, moisture-proof, mould proof, dustproof, and fixed components;

lResistance to Chemical dielectric, anti-yellowing, resistance to climate ageing.

Typical Application

9055# is suitable for bonded seal of electronic components, power module and control module, which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.

Technical Parameters

Before Curing	Appearance	Black/Transparent Fluid
	Density(25°C g/ml)	0.98±0.02
	Viscosisty(25°Ccps)	Part A 500±100:Part B:800±100
	Mixing Ratio	A:B=1:1(By weight)
	Operating Time(25°C hr)	5
	Curing time(80°C hr)	0.5
After Curing	Hardness(Shore A)	0-40
	Dielectric Strength(KV/mm)	23
	Volume Resistance(Ω.Cm)	1.0×10 15
	Permittivity(1.2MHz)	3.0
	Temperature Resistance(°C)	-60~200
	Fire Resistance	UL94-V1

(Pls note: all data of this product above in 25 °C with 55% humidity conditions. We don’t guarantee a same data if testing under different conditions, or when data was regenerated)

TECHNICAL GUIDELINES

1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.

2, Weight Ratio: part A: part B = 1:1

3, Deaeration the mixture under 0.08 MPa for 3 minutes.

4, The temperature influences the curing time of 9055. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.

Warm Tips:
1. The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.

lCondensation silicone which not completely cured or organic tin compounds

lSulphur, sulfide and sulfur rubber materials.

lAmine compounds as well as contains the amine materials.

lPewters solder flux.

2. Should be sealed storage. The mixture should be used up at once, avoid causing waste.

3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.

4. When it gets stratified after a period of storage, Please mix 9055# evenly before using, it does not affect the performance.

PACKAGE
20Kg/pail (Part A10Kg + Part B10Kg)

SHELF LIFE AND TRANSPORTATION

1. Twelve(12) months from date of shipment when stored at 24C in original unopened packages.

2. This kind of product is non-dangerous product, it can be transported as general chemicals.

3. Products exceed the storage life should be confirmed normal before using.