200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY 620# silicone rubber
payment methodL/C, T/T, Western Union
update timeSat, 23 Nov 2013 08:30:19 GMT
CAS No. HongYe silicone rubber
Purity 100%
color white
sample available
HS Code 39100000
Hardness (A°) 20±2
Mixing Ratio of silicone and catalyst 100:3
Operating time (mins 25 0C ) 30-45
Curing time(hours 25 0C) 6-8
MOQ 200kg
Min Order200 kilogram
liquid RTV-2 silicone rubber material features:
liquid RTV-2 silicone rubber material for gypsum statues mold making is white or red flowing liquid with general hardness of 22-50A°after curing. Molding silicon rubber is a kind elastic silicon rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength ,tear strength and elongation.
liquid RTV-2 silicone rubber material operations
liquid RTV-2 silicone rubber material for gypsum statues mold making operation instructions
If the customer wants to make large products and large size molds, the mold should be made of silicone rubber with high hardness. On the contrary, if the mold with fine and precision patterns, it should be made of silicon with low hardness. The amount of the curing agent depends on the actual requirements of the customer. If molds requiring fast drying and demould, more curing agent is needed; contrarily, if molds requiring slower drying and demould, less curing agent is needed.
(Note: our company does not recommend you to add silicone oil. If a special soft silicon mold or fine detailed and complex patterns products are required, 5%-10% silicone oil can be added to soften the mold for easy demould.)
The proportions and reactions of the curing agent and the silicon are listed as follows:
1. Adding curing agent 1%, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.
2. Adding curing agent 2%, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.
3. Adding curing agent 3%, the silicone can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.
4. Adding curing agent 4%, the silicone can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.
If you have any questions withliquid RTV-2 silicone rubber material, pls feel free to contact Ms Angel Yue
MSN: angelfly369(at)msn(dot)cn
Skype:angelfly369
Email:hysa(at)szrl(dot)net
Tel:0086-755-89948006
Mob: 086-18938867575
Trademanager:cn200039753
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.