Liquid silicone for Soap mould silicone

 Liquid silicone for Soap mould silicone 

Usage of  Liquid silicone for Soap mould silicone  :

For the duplication and mold making of glass crafts, lighting, candle,SOAP, culture relics duplications.

Description of   Liquid silicone for Soap mould silicone 

 Liquid silicone for molds ( Pourable silicone\Soap mould silicone ) is mainly used for toy gifts and craftwork gifts with the advantages of good tensile strength, high tear strength, high temperature resistance, high duplication times and repeated use, etc. It is suitable for small products or fine and precision products which is difficult to demould. This Liquid silicone for molds ( Pourable silicone\Soap mould silicone ) is one of the products with the highest use level in the production of craftwork gifts and the shrinkage is up to 2‰.

Applications: Poly technique, lightings, candles, and  molds in multiple pieces for large products.

Liquid silicone for molds\Pourable silicone\Soap mould silicone Standard Datasheet:

Operation Instruction for RTV-2 Liquid silicone for molds and pourable silicone and soap mould silicone:

The product is white or red flowing liquid with general hardness of 34—38A°after curing . If the customer wants to make large products and large size molds, the mold should be made of silicon rubber with high hardness. On the contrary, if  the mold with fine and precision patterns , it should be made of silicon with low hardness. The amount of the curing agent depends on the actual requirements of the customer. If molds requiring fast drying and demould, more curing agent is needed; contrarily, if molds requiring slower drying and demould, less curing agent is needed./span>

(Note: our company does not recommend you to add silicone oil. If a special soft silicon mold or fine detailed and complex patterns products are required, 5%-10% silicone oil can be added to soften the mold for easy demould.)

The proportions and reactions of the curing agent and the silicon are listed as follows:

1. Adding curing agent 1%, the silicon can still be operated within 2.5 hours and can be demoulded after 6-8 hours.

2. Adding curing agent 2%, the silicon can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.

3. Adding curing agent 3%, the silicon can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.

4. Adding curing agent 4%, the silicon can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.