200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelAddition Silicone
payment methodT/T, L/C, Westem Union
update timeTue, 05 Nov 2013 11:31:29 GMT
Color high translucent
Silicone Rubber:Curing Agent 1:1
Certification SGS,MSDS,RoHS
Material 100% silicone
Certificate SGS
Classification Chemical Auxiliary Agent
Appearance Fluid
name 966#,967#silicone rubber
Sample Free
Min Order200 kilogram
Silicone Rubber for Trademark With High Translucent
Number:
hy966 hy967
Usage:
trademark of jeans,shoes and toys.
Description:
the series of silicone rubber is divided into dispensing type hy-966 and coating type hy-967,they can not only be fabricated into trademarks independently,but also be fabricated into trademarks through cloth pressing and leather pressing.
HY-966 A/B dispensing type trademark silicone rubber belongs to liquid addition cure systerm,the amount of the curing agent can be 10% and can also be adjusted to the mixing proportion of 1:1,the curing agent is two-component high-strength liquid silicone rubber made of basic compound,cross-linking agent,catalyst,padding and additive,those materials do not contain heavy metal and aroma solvent,hence.it is not harmful to human body.
Typical curing condition:
170 degree celsius in 5 mins,prolong or shorten the curing time appropriately according to the thickness and size of the product during actual use.
using instructions:
the mixing proportion of hy966 A and hy966 B is 10:1,mix component A and component B sufficiently and evenly according to the mixing proportion before use,the process of vacuum-pumping is also needed.
Note:
the series of products must not be in contact with organisms like N.P.S etc,ionic compounds like Hg,Bi,As,etc.and alkynes, vinyl compounds,etc,to avoid the situation at the products can not be cured due to platinum catalyst poisoning,the products particularly can not be in contact with PVC which contains lead causing catalyst poisoning,some organic pigment also can slow down the curing time or cause uncured.
after hy966 A and hy966 B are mixed,the silicone rubber must be used up within 4 hours,otherwise the cross-linking and curing arises to lose effectiveness,in case of a higher surrounding temperature,more attention should be paid.
Instruction:
typical data can not be directly used for actual production guidance.please contact us for details.
Package:
general packages of hy966 and hy967 products is in 5 kg per can,20kg per pail and 200kg per barrel.
precautions:
the products can be transported as safety and non-hazardous goods since they are noninflammable with resistance to a high temperature above 300 degree celsius.
Standard Datasheet:
Item no. | HY-966 | HY-967 | ||
Component | A | B | A | B |
Appearance | Transparent | Transparent | Transparent | Transparent |
Mix ratio (%) | 10 | 1 | 10 | 1 |
Viscosity (cps) | ≥40000 | ≥35000 | ||
Pot life (H) | 1-1.5 | 1-1.5 | ||
Curing time (H) | 12-16 | 12-16 | ||
Elongation (%) | ≥400 | ≥400 | ||
Tear strength (KN/m) | ≥15 | ≥20 | ||
Hardness (A°) | Hardness can be adjusted according to the requirements of customers (20-28 A°) |