High Strength Silicone Compound for Concrete Statue Molds

  High Strength Silicone Compound for Concrete Statue Molds   

1.Mainly application of  silicone compound

silicone compound is a two part silicone rubber and curing with tin catalyst. As with a low viscosity,high tear strength and excellent duplication times,it's widely used for concrete casting,cement products casting,making molds for artificial stone,concrete crafts,cement crafts,GRC/GPR decorations,concrete statues and garden statues ect. 

2.Features of silicone compound

Good cut-growth resistance
High durometer hardness
Low shrinkage
Easy release
Room temperature cure within 24 hours
Heat-accelerable cure 

Long mold life
Highly detailed reproductions
Simplified handling

3.Technical datasheets of silicone mold making rubber rtv 638#

 Model:638#

Appearance:white/red

Viscosity(cs):22000

Hardness(A):33

Tensile strength(kgf/cm)≥35-36

Elongation break(%):≥450

Retractility(%):≤0.3

Operate time(min):30

Curing time(hours):2-4

Mixing proportion of curing agent:4%

 4.How to making concrete statue molds with silicone compound?
1. Stir the base (Part A) well beofre use (except when depending on machine ).

2. Shake the catalyst container (Part B) well before use. 

3. This is a 100 Part A to 4 Part B mixing ratio by weight.Weigh the desire amount of base into a clean mixing container.

4. Weight the proper amount of catalyst into the container. Mix the base and catalyst together by stirring with a stick until a uniform color is obtained. Scrape the container walls and bottom well to insure a thorough mix. 

5.Though it is often unnecessary to deair the material due to its low viscosity some may choose to do so. If so,place the container into a vacuum chamber and evacuate the entrapped air from the mixture using a vacuum pump capable of achieving 29 inches of mercury vacuum.The mixture will rise, crest and then collapse in the contanier. Interruption(bumping) of the vacuum may be necessary to prevent overflowing the container. Keep the mixture under full vacuum for 2-3 minutes. 

6. Bleed air slowly into the vacuum chamber. When the chamber is at atmospheric equiplibrium,remove the cover plate and take out the container. 

7.Pour the deaired material slowly in a steady stream from one end of the mould so that the material flows evenly over the pattern. This should minimize emtrapment of air bubbles under the flowing material. A mold may be poured firstly over the pattern, which will also help reduce the possibility of entrapping air on the pattern and in the cured rubber.A mold release agent may be applied on the pattern first to improve release. 

5.Shelf life of silicone compound

Twelve(12) months from date of shipment when stored at 25⁰C in the original  sealed packages.

6.Package style of silicone compound

Packed in clean 25kg/pail, 200kg/pail.

Any questions about Silicone Rubber, Leah is at your service.

TEL: 086-755-89212382

FAX: 086-755-89948030

MOBILE: 086-189 3886 7561

Website: www(dot)szrl(dot)net

E-MAIL: hyji(at)szrl(dot)net

Skype: leahchou1214

QQ: 189 3886 7561