100 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameRTV-2 silicone rubber for molds making
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelHY630#
payment methodT/T, L/C, Westem Union
update timeTue, 05 Nov 2013 13:24:47 GMT
color white
certifications RoHS.MSDS.SGS ISO9001:2000
operation way pouring and brushing
hardness 30 shore A
shrinkage low shrinkage
visicosity low visicosity
deformation no deformation
elasticity good elasticity
duplication times high duplication times
Min Order100 kilogram
Liquid Silicone for Capitals and Columns Casting feature description:
A. Workability
The base compound and curing agent are mixed and then poured into the mold to create a silicone rubber mold quickly. Workable time and cure time can be adjusted.
B. Mold-releasability
The cured rubber releases easily from the mold, so mold-release agents (soapy water, wax, etc.) are unnecessary.
C.Dimensional stability
These rubbers offer good dimensional stability, with little shrinkage.
D. Flowability
They have excellent flowability, so the original form is reproduced accurately. This includes even intricate shapes and details such as fingerprints and wood grain.
E.Heat and chemical resistance
These rubbers have outstanding resistance to heat and chemicals.
F.Deep-section curability
Moldmaking RTV silicone rubber compound cures uniformly throughout the mold, regardless of thickness
G.Non-exothermic
No heat is generated during curing, meaning no adverse effects to the original.
Liquid Silicone for Capitals and Columns Casting curing agent and silicone proportion and reaction(Under room-temperature-25C)
1.Added with 2 percent of curing agent, silicone can still flow within 1.2-1.6 hours, mold can be released in 7-8 hours.
2.Added with 3 percent of curing agent, silicone can still flow within 1-1.2 hours, mold can be released in 6-7 hours.
3.Added with 4 percent of curing agent, silicone can still flow within 40-50 minutes, mold can be released in 5-6 hours.
Operation of Liquid Silicone for Capitals and Columns Casting
1. deal with original moulds
2. brush on release agent
3. correct weigh accoring to mixng ratio
4. stir the two component evenly
5. vacuum-pumping
6. pouring
TDS of Liquid Silicone for Capitals and Columns Casting
Model:630#
Appearance:white/red
Viscosity(cs):15000-17000
Hardness(A):30
Tensile strength(kgf/cm)≥35-36
Elongation break(%):≥450
Retractility(%):≤0.3
Curing agent mixed rate(%):2-3
Operate time(min):30
Curing time(hours):2-4
Mixing proportion of curing agent:4%
Any questions of Silicone Rubber, please feel free to contact Miss Leah:
TEL: 086-755-89212382
FAX: 086-755-89948030
MOBILE: 086-189 3886 7561
Website: www(dot)szrl(dot)net
E-MAIL: hyji(at)szrl(dot)net
Skype: leahchou1214
QQ: 189 3886 7561
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.