Tin (Condensation-Cure) Silicone Mold Rubbers

Tin (Condensation-Cure) Silicone Mold Rubbers are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.

Tin (Condensation-Cure) Silicone Mold Rubbers is primarily intended for the reproduction of plate engrave ,human replica;for the mold making of poly resin crafts, PU crafts, PU resin crafts,gypsum crafts,unsaturated resin crafts,lighting and candles crafts,soap mold,plastic toy,stationery gifts crafts industry,a large statue Buddha,furniture,furniture decorative materials,statues Buddha,artifacts copied,building decoration materials,large-scale cement mold,artificial fossils Factory,Europe component factory,simulation landscapes,animals and plants sculpture,sandstone crafts and so on.

Some of the materials you can cast into a silicone mold are:
• Urethane Plastic
• Urethane Rubber
• Epoxy
• Polyester
• Fiberglass Resign
• Plaster
• Soap
• Wax
• Low melt metals (up to 400 degrees Max)
• HydroCal White
• UltraCal 30
• Rigid Foam

• concrete statue mold

/FDA certificate,no toxicity.

/Good fluidity and good operability and good for pouring method.
/Excellent mechanical properties, in particular tear strength and tensile strength.
/Excellent flexibility

/High temperature resistance, high duplication times and repeated use.
 

1.The cast pouring, for example:
Prepare a frame, fix the prototype for copy into the frame, (if the prototype’s material is glass or ceramic, the release agent is necessary to prevent sticking.
2. Take 100 part A and 4 part B,mix themevenly.
3.Vacuum defoaming in 1~3 min,inject the rubber into the type box, then vacuum defoaming again, curing 24 hours in nature room temperature, use it after demold.
4. Demold after 3 hours’ room temperature curing, and then use it after 24 hours’ keep mold under the same condition.

Firstly,the silicone rubber and catalyst must be mix evenly,mixing for 5-6 minutes,if you do not mix evenly,it will cause one part is dry but other part is wet.

Secondly,if you have a vacuumed machine,that's will be perfect, vacuuming mixed silicone for 5-6 minutes,there will not have bubble.

Thirdly,the silicone mould need 24 hours to complete dry,so when you finished the silicone mould,please after 24 hours later bring into production.
I believe that the silicone mould will be perfect if you pay attention to these points.

Delivery terms:FOB,CFR,CIF

Exchange rate:1USD=6.20RMB
Packing:5kg/pail,25kg/pail,200kg/pail
Delivery time is within 3 days after getting your bank receipt.
Payment Terms: T/T 100% in advance,L/C,Western Union
Mind order quantity(MOQ):100KG

Transport: by sea or by air

Shelf life:12 months under room temperature not open