RTV-2 silicone rubber for tire mould design

FOB Price

US $10.90
100 - 40,000 kilogram
US $6.70
40,001 - 999,999 kilogram

group nameRTV-2 silicone rubber for molds making
Min Order100 kilogram
brand nameHong Ye silicone rubber
modelHy 528#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 15:27:08 GMT

contact supplier

Paramtents

Application Mold making silicone rubber
H.S. code 39100000
Shelf life 12 months
Appearance Liquid
Curing agent / Catalyst 4% for free of charged
Mixing ratio 100:5 / 100:4/ 100:3
Sample Free
Package Vacuum packing
Certificate FDA,SGS, RoHS, MSDS, ISO9001:2000

Packging & Delivery

Min Order100 kilogram

Briefing

RTV-2 silicone rubber for tire mould design :
low shrinkage
good fluidity,
fast curing speed,
high tearing strength

Detailed

***Welcome to Hong Ye Jie Technology Co., Ltd***
If you have any question, Pls feel free to ask ~

RTV-2 silicone rubber for tire mould design

Enjoy Good quality but lower price !!!

1.Application

*cultural relic duplication,

*architectural decoration,

*resin crafts,

*lighting ornaments,

*candles, statues,

*model design,

*product exploitation, etc.

2.Advantage

*low shrinkage (less than 0.1% )

*high tensile and tear strength with high copy times

*easy for operation (mixing ratio at 1:1 /10:1)

*very good flow and easy for pouring operation

*Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat

3.Features

liquid molding silicone rubber, silicon rubber are generally named two -component room temperature vulcanization silicone rubber,

a kind elastic silicone rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion.

RTV-2 silicone rubber for tire mould design

4.Operation instructions

car tire mold making silicone rubber are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2-3% curing agent, they can still be operated within 30 minutes, but will be formed after 2-3 hours. With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.

5.Datasheets

Model	528#
Appearance	white
Mixing proportion of curing agent (%)	4-5%
Operating time (mins 25 0 C )	30-60
Curing time(hours 25 0 C )	4
Hardness (A°)	28-30
Density ( g/cm 3 )	1.08
Viscosity (mPas - 25 0 C )	28000-32000
Tensile-strength(kgf /cm 2 )	4.0-4.4
Tear-strength (kgf /cm )	22-26
Elongation-break( % )	360-400
Retractility( % )	≤0.3