liquid Addition (Platinum) Cure RTV-2 silicone for molding

FOB Price

US $12.30
200 - 40,000 kilogram
US $9.80
40,001 - 999,999 kilogram

group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE610
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 15:46:27 GMT

contact supplier

Paramtents

Color Translucent
Certificate SGS,RoHS,ISO
Mixing Ratio 1:1
Application size of mold small/
Recommend operation way pouring
Retractility(%) ≤0.1
shelf life 12 months
cure life 3~5 hours
pot life 30~50 mins
origin Guangdong, China

Packging & Delivery

Min Order200 kilogram

Briefing

- High fluidity
- Excellent reproduction of details
- Good mechanical properties
- Low linear shrinkage
- No release toxic

Detailed

addition cure silicone

liquid Addition (Platinum) Cure RTV-2 silicone for molding

addition cure silicone application:

--Rapid prototyping( urethane casting/ silicone tooling / vacuum casting)

--GRC and Concrete molding

--PU resin casting

--General mold making

--Superior manual mold design

--Food grade molding application

addition cure silicone E610 compounds for moldmaking are suitable for mold masters for molding with polyester resin, epoxy resin, urethane foam, wax, plaster, and low-melt-point metal alloys with small size. These RTV rubber compounds allow accurate reproduction of the shape of the original. They are easy to use and are thus used widely in industrial applications, as well as by hobbyists looking to create the perfect replica.

addition cure silicone description:

--No release of toxic substances during and after curing
--High resistance to inorganic chemicals and UV rays
--Good release properties with organic resins and gypsum

--Almost nil shrinkage

addition cure silicone E610 DATASHEET

Model	E610#
Appearance	Translucent
Mixing Ratio	1:1
Operating time (Mins 25°C)	30 - 50
Curing time (Mins 25°C)	120 - 240
Curing time (Mins 60°C)	20 - 30
Hardness (A°)	10±2
Density ( g/cm 3 )	1.08
Viscosity (CS) (Part A)	10000 ± 5000
Viscosity (CS) (Part B)	2000 ± 500
Viscosity (CS) (After mixed)	6000 ± 2000
Tensile-strength( kgf /cm2 )	50 ± 10
Tear-strength (kgf /cm2 )	25 ± 2
Elongation-break(%)	500 ± 50
Retractility(%)	≤0.1