group nameRTV-2 silicone rubber for molds making
Min Order100 kilogram
brand nameHong Ye silicone rubber
model640 silicone rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 16:12:21 GMT
color blue/red/white/yellow/white
Mixing proportion of curing agent (%) 2%-3%
Operating time (hour 25 0C ) 0.5
Curing time(hours 25 0C) 6-8
Hardness (A°) 38-40
Density ( g/cm 3) 1.09
Viscosity (CPS 25 0C) 18000-25000
Tensile-strength(kgf /cm2 ) ≥37
Tear-strength (kgf /cm) ≥26
Elongation-break(%) ≥ 500
Min Order100 kilogram
FEATURES of Liquid silicone rubber:
Two-part silicon rubber:flowable liquid silicon and curing agent.
Cures at room temperature within 6-8 hours.
An exceptional fluidity and good operability, easy to demold.
Good tensile and tear strength, low shrinkage.
High duplication times.
Liquid Silicon Rubber Series
RTV-2 Room temperature silicone rubber
Model: HY-640
Usage: Silicon rubber for large products like PU/poly resin, unsaturated resin, plaster decoration, and gypsums crafts, toys, soap, statuary ,casting molds making,etc.
Model | 640# |
Appearance | white |
Mixing proportion of curing agent (%) | 4% |
Operating time (mins 25 0C ) | 30-45 |
Curing time(hours 25 0C) | 6-8 |
Hardness (A°) | 38-40 |
Density ( g/cm 3 ) | 1.08 |
Viscosity (mPas -25 0C) | 10000 |
Tensile-strength(kgf /cm2 ) | ≥39 |
Tear-strength (kgf /cm ) | ≥21 |
Elongation-break(%) | ≥ 390 |
USERS INSTRUCTION of Liquid silicone rubber:
Liquid silicone rubber are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability.When mixed with 3%-5% curing agent, they can still be operated within 30 minutes,but will be formed after 6-8 hours.With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.
This product is a white or red flowable liquid with a hardness of 22-50A° when cured. If large products and therefore multiple-piece molds are needed by customers, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise.
(Note:we do not recommend silicon oil. For special soft mold or molds with complex pattern or fine details, 5%-10% silicon oil can be added to condition the flexibility of the mold for convenience of release)
TECHNICAL GUIDELINES of Liquid silicone rubber:
1. Stir the base (Part A) well beofre use (except when depending on machine ).
2. Shake the catalyst container (Part B) well before use.
3. This is a 100 Part A to 3-5 Part B mixing ratio by weight.Weigh the desire amount of base into a clean mixing container.
4. Weight the proper amount of catalyst into the container. Mix the base and catalyst together by stirring with a stick until a uniform color is obtained. Scrape the container walls and bottom well to insure a thorough mix.
5. Though it is often unnecessary to deair the material due to its low viscosity some may choose to do so. If so,place the container into a vacuum chamber and evacuate the entrapped air from the mixture using a vacuum pump capable of achieving 29 inches of mercury vacuum.The mixture will rise, crest and then collapse in the contanier. Interruption(bumping) of the vacuum may be necessary to prevent overflowing the container. Keep the mixture under full vacuum for 2-3 minutes.
6. Bleed air slowly into the vacuum chamber. When the chamber is at atmospheric equiplibrium,remove the cover plate and take out the container.
7. Pour the deaired material slowly in a steady stream from one end of the mould so that the material flows evenly over the pattern. This should minimize emtrapment of air bubbles under the flowing material. A”ready”mold may be poured firstly over the pattern, which will also help reduce the possibility of entrapping air on the pattern and in the cured rubber.A mold release agent may be applied on the pattern first to improve release.
8. Allow the rubber to cure for 2-4 hours at 24C before removing the cured rubber mold from the pattern. Heat acceleration not recommended with this product.
9. For best results, allow the mold to air cure an additional 24 hours before using it in production.
SHELF LIFE of Liquid silicone rubber:
Twelve(12) months from date of shipment when stored at 250C in the original sealed packages.
PACKAGE of condensation silicone rubber for mold making:
Packed in clean 25kg/pail, 200kg/pail.
FIRST AID:
Inhalation: Remove source(s) of contamination and move victim to fresh air. Contact physician immediately.
Eye Contact: Flush eyes with plenty of water. If irritation persists, seek medical attention.
Skin Contact: In case of skin contact, wash thoroughly with soap and water; remove contaminated clothing and launder before reuse; seek medical attention if rash develops.
Ingestion: Do not indeuce vomiting unless instructed by a physician.Contact physicain immediatedly.
After first aid, get appropriate in-plant,paramedic,or community medical support.
If you have any questions with Liquid silicone rubber, pls feel free to contact Ms Aimee
MSN: aimeezhou055722(at)hotmail(dot)com
Skype:aimee055722
Email:hysz(at)szrl(dot)net
Tel:0086-755-89948006
Mob: 086-18938867541
Trademanager:cn200039753
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.