200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE620/625/630# Silicone Rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 16:47:21 GMT
An exceptional fluidity Good operability
Category Food grade silicone
Application Making molds for candy & chocolate
Mix ratio 1:1
Certificate Rohs, SGS
Operation time 30-45 mins
Curing time 4-6 hours
MOQ 200 KG
Package 20 kg/drum, 200 kg/drum
Shelf life 12 months
Min Order200 kilogram
Industry Stone Moulds Addition Cured Silicone Performance:
Industry Stone Moulds Addition Cured Silicones,Our E series rtv-2 addition cure mold making silicone is with the all the advantage of rtv-2 condensation cure silicone rubber, but is also featured with lower shrinkage and low viscosity, good fluidity; Without releasing any by-product with low molecular weight, and it's cured from top to bottom, from the inside and outside simultaneously, so it will be deeply-cured. The E sereise addition cure silicone will not meet the problem of degradation or sticky molds because of the existence of by-product of small molecules under certain conditions, (such as closed, high temperature).it's very suitable for all kinds of mold with a variety of sizes, shapes and large sized plaster, cement,ect molds making.
Industry Stone Moulds Addition Cured Silicone Main Applications:
Industry Stone Moulds Addition Cured Silicones,This product can be used in not only the field of common RTV-2 moldmaking silicone. As the vulcanizing reactions of addition cure silicone is fundamentally different from tin cure silicone’s, it has no problem of deep vulcanize or reverse reaction, ect problem. Therefore, our addition cure silicone is particularly applicable for large stones, plaster and cement product replication. It features with lower viscosity, high strength , good fluidity, can also be very suitable for precision complex pattern of the original copy.
Technical Datasheets for Industry Stone Moulds Addition Cured Silicone
MODEL | COMPOUNENT | BEFORE CURING | AFTER CURING | ||||||
Appearance | A Viscosity cP(25°C) | B hardness (shore A) | C Pot life min(25°C) | D initial curing (h) | Tensil- strength (Mpa) | Tear- strength (kN/m) | Elongation (%) | ||
E620 | A+B | translucent | 27000±5000 3500±1000 6000±1000 | A+B (1:1) 20±2 | A+B (1:1) 30±10
| A+B(1:1) 4±1 | A+B (1:1) ≥2.5 | A+B (1:1) ≥12 | A+B (1:1) ≥400 |
E625# | A+B | translucent s | 27000±5000 3500±1000 6000±1000 | A+B (1:1) 25±2 | A+B (1:1) 30±10 | A+B(1:1) 4±1 | A+B (1:1) ≥4.0 | A+B (1:1) ≥12 | A+B (1:1) ≥300 |
E630# | A+B | translucent | 27000±5000 3500±1000 6000±1000 | A+B (1:1) 30±2 | A+B (1:1) 30±10 | A+B(1:1) 4±1 | A+B (1:1) ≥4.0 | A+B (1:1) ≥10 | A+B (1:1) ≥300 |
Any questions,please feel free to contact Ms Judy
TEL: 086-755-89948019
FAX: 086-755-89948030
MOBILE:086-18938867591
QQ: 18938867591
Skype: judy.zhao723
Website: www(dot)szrl(dot)net
contact: hyja at szrl dot net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.