RTV silicone for soap toys making molds

RTV silicone rubberused for statues, prefabricated concrete, rosettes, cornices, fountains and garden articles, sanitary fixtures, decorative pottery, giftware, industrial equipment, decorative candles, gaskets, mechanical components, but also soles for footwear, archaeological findings or automotive prototypes mold making.

RTV siliconeis a two-part silicone rubber; It has an easy release, high elongation, minimal shrinkage, long work time.

Silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.

RTV silicone for soap toys making molds.

Model: 638#  rtv silicone rubber
Appearance: White
Viscosity (CS): 25000
Hardness (A): 20-22
Tensile strength(kgf/cm2 ) ≥35
Tear strength (kgf /cm): ≥25
Elongation break(%): ≥500
Retractility (%): ≤0.2
Curing agent mixed rate (%): 2-3
Operate time (min): 30
Curing time (hours): 2-4

Model: 728#   rtv silicone rubber
Appearance: White
Viscosity (CS): 18000
Hardness (A): 25
Tensile strength(kgf/cm2 ) ≥35
Tear strength (kgf /cm): ≥22
Elongation break(%): ≥320
Retractility (%): ≤0.2
Curing agent mixed rate (%): 2-3
Operate time (min): 30
Curing time (hours): 2-4

Model: 788#   rtv silicone rubber
Appearance: White
Viscosity (CS): 18000-25000
Hardness (A): 28-32
Tensile strength(kgf/cm2 ) ≥35
Tear strength (kgf /cm): ≥20
Elongation break(%): ≥470
Retractility (%): ≤0.2
Curing agent mixed rate (%): 2-3
Operate time (min): 30
Curing time (hours): 2-4

Features of RTV silicone for soap toys making molds:
(1) Silicon rubber for pad printing with SGS and ROSH approval
(2) Curing agent arrange together as free charged
(3) In liquid form and in various colors
(4) With an exceptional fluidity and good operability.
(5) Temperature and deformation resistance as well as low shrinkage.
(6) High duplication times.
(7) Sample orders are available
(8) MOQ: 100KG