200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
model625#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 17:25:06 GMT
Color White
Mixing ratio 100:4
Catalyst 4% for free
Shelf life 12 month
Hardness Shore A 25
Packing 25kg/pail
Payment T/T
Certification REACH,ROHS,ISO
Feature High duplication times rubber
Characteristic High tear and tensile strength
Min Order200 kilogram
High strength RTV rubber silicone
Mainly application of High strength RTV rubber silicone
High strength RTV rubber silicone is a two part silicone rubber and curing with tin catalyst. As with a low viscosity, high strength and excellent duplication times.
it's widely used for
concrete casting
cement products casting
making silicone molds for artificial stone
concrete statue molds,garden statue molds
stone molds
cement crafts
GRC/GPR decorations,ect.
Features of High strength RTV rubber silicone
a.low viscosity
b.easy operation
c.long shelf life over 12 months
d.good tear strength and low shrinkage
e.curing at room temperature within 2-4hours
f.high duplication times and no deformation
How to make a silicone mold with High strength RTV rubber silicone
a. clear and smooth original moulds
b. brush on release agent
c. correct weigh accoring to the mixng ratio
d stir the two parts evenly
e. vacuum-pumping less than 10min
f. pouring or brushing
(Note: We are not recommend you to add silicone oil. If a special soft silicon mold or fine detailed and complex patterns products are required, 5%-10% silicone oil can be added to soften the mold for easy demould.)
If you have any questions about High strength RTV rubber silicone or any inquiry, please do not hesitate to contact with Ms. Moe
Mobile: +86-18938867514
Tel: +86-755-89948019
Fax: +86-755-89948030 .
TDS of High strength RTV rubber silicone
Model | 638# | 630# | 625# | 620# |
Appearance | white | white | white | white |
Mixing proportion of curing agent (%) | 5% | 5% | 5% | 5% |
Operating time (mins 25 0C ) | 40~70 | 60~90 | 40~70 | 30~50 |
Curing time(hours 25 0C) | 4~7 | 5~7 | 4~7 | 3~5 |
Hardness (A°) | 36±2 | 30±2 | 25±2 | 20±2 |
Viscosity (Mpas -25 0C) | 30000~38000 | 27000~32000 | 17000~19000 | 12000~14000 |
Tensile-strength(Mpa) | ≥4.50 | ≥4.2 | ≥3.2 | ≥2.8 |
Tear-strength (KN/m) | ≥30 | ≥30 | ≥27 | ≥32 |
Elongation-break(%) | ≥ 420 | ≥ 440 | ≥ 440 | ≥ 420 |
Linear Shrinkage (%) | ≤0.3 | ≤0.3 | ≤0.3 | ≤0.3 |