200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelsilicone rubber E-series
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 17:31:55 GMT
color any
Packages 25kgs and 200kgs per drum
Application For moulds making
certificate RoHS, MSDS, SGS, ISO9001:2000
sample available
mix ratio 1:1
shelf life 10 month
MOQ 200 kgs
HS code 3910 0000
package 20 and 200 kgs/drum
Min Order200 kilogram
Delivery Time: within 3 days after payment confirmed in our bank.
Payment Terms: L/C,T/T
addition silicone rubber Description
addition silicone rubberis generally named two-components silicone rubber, Part A and part B. It features an exceptional fluidity and good operability. The mixing ratio is 1:1,mainly be suitable for making molds application.
addition silicone rubber Applications
addition silicone rubbercould be mainly used for making concrete stones, wax molds, PU molds, resin molds, gypsum casting, candle molding and chocolate , candy and any other FDA food product mold making,prototyping etc.
Instruction of addition silicone rubber
addition silicone rubber are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2-3% curing agent, they can still be operated within 30 minutes, but will be formed after 2-3 hours. With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.
Features of Flexible addition silicone rubber
(1)high tensile & tear strength
(2) Low linear shrinkage
(3)free Curing agent
(4)brushing & pouring
(5) high duplication times
Technique Data Sheet of HY-E series addition silicone rubber
Product | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 20±2 | 25±2 | 30±2 | 42±2 |
Mix ratio(A:B) | 1:1/10:1 | 1:1/10:1 | 1:1/10:1 | 1:1/10:1 |
Viscocity Part A(mPa.s) | 23000±2000 | 27000±2000 | 25000±2000 | 30000±2000 |
Viscocity Part B(mPa.s) | 3500±500 | 3500±500 | 2400±500 | 6000±500 |
Tensile strength (kgf/cm2) | 45±5 | 48±5 | 50±5 | 65±5 |
Tear-strength (kN/m) | 20±2 | 22±2 | 18±2 | 16±2 |
Elongation(%) | 500±50 | 500±50 | 450±50 | 450±50 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 110-20mins(60°C) | 3-4hrs(25°C) 110-20mins(60°C) | 3-4hrs(25°C) 110-20mins(60°C) | 3-4hrs(25°C) 1 110-20mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 |
(Note: Other hardness is adjustable)
Any questions of railing Molds addition silicone rubber, please feel free to contact Kaimi:
FAX: 086-755-89948030
MOBILE:086-18938867528
Website: www(dot)szrl(dot)net
E-MAIL: hyju(at)szrl(dot)net
skype:hyjiangying
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.