group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelAddition cure silicone E642#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 17:45:17 GMT
Available color Translucent
Certifications RoHS.MSDS.SGS ISO9001:2000
Operation way brushing
Hardness 42 shore A
Curing time 20 - 30min
Mixing proportion of curing agent 1:1
Operating time 20-30min
Viscosity (MPas -25 0C) 30000 ± 5000(part A),5000 ± 500(part B)
Tensile-strength(kgf /cm2 ) 80 ± 5
Min Order200 kilogram
Mainly application of Pourable Silicone Moldmaking Rubber
Pourable Silicone Moldmaking Rubber is a two part silicone rubber and curing with tin catalyst. As with a low viscosity, high strength and excellent duplication times, it's widely used for concrete casting and cement products casting, making silicone molds for artificial stone, concrete statue molds, garden statue molds, stone molds, cement crafts, GRC/GPR decorations, ect.
The quality of our rtv silicone rubber is similar with Dow corning silicone, Wacker silicone, smooth on silicone, but the prices of our silicone rubber is more competitive than them.
Features of Pourable Silicone Moldmaking Rubber
a. low viscosity
b. easy operation
c.long shelf life over 12 months
d. high strength and low shrinkage
e. curing at room temperature within 2-4hours
f. high duplication times and no deformation
Instructions for Use pourable silicone moldmaking rubber
It is recommended to homogeneously mix the base compounds before use.
Mixing:
Select a mixing container 4-5 times larger than the total volume of material to be mixed.
Weigh out the selected RTV and beta catalyst. Stir for several minutes scraping the
sides and bottom of the container carefully to produce a homogeneous mixture. When
using power mixers, avoid excessive speeds, which could entrap large amounts of air or
cause overheating of the mixture, resulting in shorter pot life.
The air entrapped in the mixing step needs to be removed to eliminate voids in the cure
product. This can be done by exposing the material to a vacuum of 10-20 mbar. The
material will expand, crest and reduce to about the original level. Degassing is usually
complete about two minutes after frothing ceases.
Automatic equipment designed to meter, mix and dispense a two-component silicone
liquid elastomer will add convenience to continuous large scale operations.
Curing:
After mixing the selected RTV/Beta combination, the material will cure at room
temperature. Selection of the Beta will determine cure speed, the work life as well as the
demoulding time.
The system is sensitive to changes in heat and humidity and therefore variations in cure
speed may be seen if one or both variables are changed.
Handling and Safety Material Safety Data Sheets are available upon request.
SHELF LIFE: Twelve (12) months from date of shipment when stored at 24°C in original unopened packages.
PACKAGE: Packed in clean 20kg/pail, 200kg/pail.
Any questions about Silicone Rubber, Leah is at your service.
TEL: 086-755-89212382
FAX: 086-755-89948030
MOBILE: 086-189 3886 7561
Website: www(dot)szrl(dot)net
E-MAIL: hyji(at)szrl(dot)net
Skype: leahchou1214
QQ: 189 3886 7561
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.