Low shrinkage and no deformation silicone for tire molding

FOB Price

US $7.60
200 - 40,000 kilogram
US $5.60
40,001 - 999,999 kilogram

group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-620# Silicone Rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 18:23:49 GMT

contact supplier

Paramtents

Classification Catalyst
Application Mould Making Materials
colour accorfing to customers requirements
certificates FDA SGS RoHS
appearance two parts fluid
sample free
package 25kg/drum
HS code 39100000
shelflife 12month
Port shenzhen
applicatin tire mold making

Packging & Delivery

Min Order200 kilogram

Briefing

1.exceptional fluidity
2. good operability

Detailed

Low shrinkage and no deformation silicone for tire molding

Description of Low shrinkage and no deformation silicone

Low shrinkage tire molding silicone is generally named two-components silicone rubber, Part A and part B. It features an exceptional fluidity and good operability. The mixing ratio is 1:1 (10:1),mainly be suitable for making molds application.

Typical Applications of Low shrinkage and no deformation silicone

Low shrinkage tire molding silicone could be mainly used for making concrete stones, wax molds, PU molds, resin molds, gypsum casting, candle molding and chocolate , candy and any other FDA food product mold making,prototyping etc.

Low shrinkage tire molding silicone is has been used for years to make tire pattern molds .

Low shrinkage and no deformation silicone for tire molding

Characteristics of Low shrinkage and no deformation silicone

*low shrinkage (less than 0.1% )

*high tensile and tear strength with high copy times

*easy for operation (mixing ratio at 1:1 /10:1)

*very good flow and easy for pouring operation

*Fast and non-shrink cure at room temperature which can be accelerated considerably by the application of heat

Low shrinkage and no deformation silicone for tire molding

Low shrinkage and no deformation siliconeTechnical Parameters

Product	E-620
Appearance	Translucent
Hardness(shore A)	20±2
Mix ratio(A:B)	1:1/10:1
Viscocity Part A(mPa.s)	23000±2000
Viscocity Part B(mPa.s)	3500±500
Tensile strength (kgf/cm2)	45±5
Tear-strength (kN/m)	20±2
Elongation(%)	500±50
Pot life/working time (mins)	30-40
Curing time/setting time (hrs)	3-4hrs(25°C) 110-20mins(60°C)
Shrinkage rate (%)	0.1

(Please note: the above data for this product in 25°C temperature, 55percent humidity conditions, for reference. The accurate data is measured by customers when using.)

Low shrinkage and no deformation silicone for tire molding