200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-E series
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 18:39:13 GMT
Certificate ISO9001:2000,FDA
Colour White/translucent/any color
Hardness 40-45 Shore A
Purity 100%
Application Molding silicone rubber
Sample Free
Technical support Free
EINECS No 39100000
Transportation By sea or by air
Min Order200 kilogram
RTV mold making addition silicone are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage.
The mixing ratio between Part A and Part B can be 10:1 or 1:1.
RTV-2 Moulding Silicone Rubber for resin/concrete application :
· Rapid prototyping (urethane casting/silicone tooling/vacuum casting)
· GRC and Concrete moulding
· PU resin casting
· General Mouldmaking
· Superior manual mold design
RTV-2 Moulding Silicone Rubber for resin/concrete main properties :
· almost nil shrinkage
· high chemical resistance to aggressive components of some types of resins
· good tear strength (this feature ensures higher resistance to wearing and shearing)
· high degree of precision in reproduction
· high dimensional stability over time and non-deformability
· high resistance to high temperatures and ageing (resit to -60-200°C)
· excellent non-stick effect
· environmental, odorless and nontoxic
E-series Translucent RTV-2 Addition silicone rubber standard datasheet (25°C)
(The mixing ratio of part A and part B can be adjusted to 1:1or 10:1)
Product | E-615 | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 15±2 | 20±2 | 25±2 | 30±2 | 40±2 |
Mix ratio(A:B) | 1:1 | 1:1 | 1:1 | 1:1 | 10:1 |
Viscocity Part A(mPa.s) | 9000±2000 | 11000±2000 | 15000±2000 | 20000±2000 | 55000±2000 |
Viscocity Part B(mPa.s) | 1900±500 | 1900±500 | 1800±500 | 2400±500 | 150±50 |
Tensile strength (MPa) | 6.2 | 6.5 | 6.7 | 7.2 | 7.6 |
Tear-strength (kN/m) | 25 | 26 | 23 | 24 | 22 |
Elongation(%) | 569 | 581 | 480 | 440 | 450 |
Density | 1.05 | 1.05 | 1.07 | 1.13 | 1.14 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 20-30mins(60°C) | 6-8hrs(25°C) 30-50mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
Package:
For getting further information about our platinum /addition cure molding silicone rubber material, PLS contact Miss.Kelly,
E-mail: hyjm(at)szrl(dot)net
MSN:kelly6in(at)hotmail(dot)com
Skype:kelly619106
Tel: 086-18938867564