Electronic Potting Compound silicone rubber

FOB Price

US $16.00
200 - 40,000 milligram
US $6.00
40,001 - 999,999 milligram

group nameelectronic potting silicone rubber
Min Order200 milligram
brand nameHong Ye silicone rubber
modelHY-9055
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:30:13 GMT

contact supplier

Paramtents

colour white
Brand Hongye silicoen rubber
Certification SGS,MSDS,RoHS
Port Shenzhen

Packging & Delivery

Min Order200 milligram

Briefing

RTV-2 Silicone is a newly insulating material silicon of silicon compounds.
It cures without heat, corrosion and just with lit

Detailed

Product Feature
RTV-2 Silicone is a newly insulating materialsilicon of silicon compounds.
It cures without heat, corrosion and just with little shrinkage. It can be applied to the sealing and pouring of various electronic components, and then forming insulation system.
Features:

l Room temperature vulcanize, and easy to operate;

l Maintain flexibility at a wide temperature range, and excellent insulation performance;

l Waterproofing, moisture-proof, mouldproof, dustproof, and fixed components;

l Resistance to Chemical dielectric, anti-yellowing, resistance to climate ageing.

Typical Application

9301 is suitable for bonded seal of electronic components, power module and control module, which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.

Technical Parameters

Before Curing	Appearence	Black/Transparent Fluid
	Density(25°C g/ml)	0.98±0.02
	Viscosisty(25°Ccps)	Part A 500±100:Part B:800±100
	Mixing Ratio	A:B=1:1(By weight)
	Operating Time(25°C hr)	5
	Curing time(80°C hr)	0.5
After Curing	Hardness(Shore A)	0-40
	Dielectric Strength(KV/mm)	23
	Volume Resistance(Ω.Cm)	1.0×10 15
	Permittivity(1.2MHz)	3.0
	Temperature Resistence(°C)	-60~200
	Fire Resistance	UL94-V1

(Pls note: all data of this product above in 25 °C with 55% humidity conditions. We don’t guarantee a same data if testing under different conditions, or when data was regenerated)

Electronic Potting Compound silicone rubber

TECHNICAL GUIDELINES

1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.

2, Weight Ratio: part A: part B = 1:1

3, Deaeration the mixture under 0.08 MPa for 3 minutes.

4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.

Warm Tips:
1.The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.

l Condensation silicone which not completely cured or organic tin compounds

l Sulphur, sulfide and sulfur rubber materials.

l Amine compounds as well as contains the amine materials.

l Pewters solder flux.

2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.

3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.

4. When it gets stratified after a period of storage, Please mix 9301 evenly before using, it does not affect the performance.

PACKAGE
20Kg/pail (Part A10Kg + Part B10Kg)

SHELF LIFE AND TRANSPORTATION

1. Twelve(12) months from date of shipment when stored at 24C in original unopened packages.

2. This kind of product is non-dangerous product, it can be transported as general chemicals.

3. Products exceed the storage life should be confirmed normal before using.

For further information ,pls don't hesitate to contact Ms Sabrina:

Tel:+86075589212382
Mobil:+8618938867574
Email:hyse(at)szrl(dot)com
Skype:sabrina369488

Web site:http://www(dot)szrl(dot)net