group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-210 silicone rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:43:52 GMT
Certificate ISO9001:2000
Purity 100%
Appearance transparent
MOQ 200KG
package 25kg/drum 200kg/drum
HS Code 39100000
color any corlor
Payment Terms L/C,T/T, Western Union
Min Order200 kilogram
Liquid electronic compound silicon rubber
Usage of Liquid electronic compound silicon rubber:
Filling for LED,LCD electronic display, circuit board.
Description of Liquid electronic compound silicon rubber
Liquid electronic compound silicon rubber is condensation silicone potting compound in two parts with low viscosity. It can be cured completely at room temperature. HY 210 works on the surface of material as PC(Poly-carbonate),ABS,PP,PVC as to its superior bonding feature. It is also applicable for insulation, waterproof and bonding of electronics parts. It meets the requirements of European RoHs.
Typical Application of Liquid electronic compound silicon rubber
-Potting for Protection of general electronic module.
-Outdoor protection for LED screen.
Technical Parameters of Liquid electronic compound silicon rubber
Properties index | Part A | Part B | |
Before Curing
| Appearance | Transparent fluid | Colorless/yellowish fluid |
Viscosity(cps) | 2500±500 | - | |
Features when operation | Mixing Ratio(By weight) | 10:1 | |
Operating Time(25°C /min) | 20~30 | ||
Curing time(hr,basically cured) | 3 | ||
Curing time(hr,perfectly cured) | 24 | ||
Hardness(shore A) | 15±3 | ||
After Curing | Thermal Conductivity[W(m·K)] | ≥0.2 | |
Dielectric Strength(kV/mm) | ≥25 | ||
Dielectric permittivity(1.2MHz) | 3.0~3.3 | ||
Volume resistivity(Ω·cm) | ≥1.0×1016 | ||
Fire Resistance | 94-V1 |
(Pls noet:all data of this product above in 25°C with 55% humidity conditions. We don't
guarantee a same date if testing under different conditions, or when data was regenerated)
Warm Tips of Liquid electronic compound silicon rubber:
1.Sealing package for storage. The mixture should be used up at once to avoid wasting.
2. Silicone belongs to non-dangerous goods, but keeps away form mouth and eyes.
3. When it gets stratified after a period of storage, please mix HY 210 evenly before using, it does not affect the performance.
Package of Liquid electronic compound silicon rubber:
HY210: 22kg/set (Part A 20kg + Part B 2kg)
Shelf life and transportation of Liquid electronic compound silicon rubber
1.Twelve(12) months when stored at 24°C in original unopened packages.
2. This kind of product is non-dangerous product; it can be transported as
general chemicals.
3. Products exceed the storage life should be confirmed normal before using.
Technical guidelines of Liquid electronic compound silicon rubber
1.Pls put part A and B in separate container and stir evenly before mixing the two
parts together.
2. Weight Ratio: part A:part B = 10:1
3.Bubble release if necessary , Deaeration the mixture under 0.08 MPa for 3 minutes.
4. HY210 is cured at room temperature, so pls put it under room temperature after pouring. It comes to next process when basically cured, and it takes about 24 hours for completely cured.
(Kindly note: Temperature and Humidity with tremendous influences for curing of HY-210)
Any more information abt Liquid electronic compound silicon rubber , pls feel free to contact Ms. Bella:
Mobile: 0086-18938867572
Tel: 0086-755-89948006
Fax: 0086-755-89948030
Website: : www (dot) szrl (dot) net
Email:hysi(@)szrl(dot)net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.