200 - 40,000 kilogram
40,001 - 999,999 kilogram
group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY9055
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:44:08 GMT
color white
sample available
HS code 39100000
feature liquild
normal packing 25kgs per drum
shelf life one year
MOQ 200kgs
delievy within 3 days
certifaicate RoHS MSDS SGS ISO9001:2008
Min Order200 kilogram
Typical Application of Addition thermal conducted silicone HY- 9055
9055 is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
Product Feature of Addition thermal conducted silicone HY- 9055
It can be applied to the sealing and pouring of various electronic components, and then forming insulation system with no corrosion and negligible shrinkage.
Technical Parameters of Addition thermal conducted silicone HY- 9055
Specification | Part A | Part B | |
Before Curing
| Appearance | Dark Grey Fluid | White Fluid |
Viscosity(cps) | 2500±500 | 2500±500 | |
Operating Performance | Part A:Part (By weight) | 1:1 | |
Viscosity after mixing (cps) | 2000~3000 | ||
Operating Time (min) | 120 | ||
Curing Time (min, 25°C) | 480 | ||
Curing Time (min, 80°C) | 20 | ||
After Curing | Hardness (shore A) | 55±5 | |
Heat Conductivity [W(m·K)] | ≥0.8 | ||
Dielectric Strength(kV/mm) | ≥25 | ||
Permittivity(1.2MHz) | 3.0~3.3 | ||
Volume Resistance(Ω·cm) | ≥1.0×1016 | ||
Linear Expansion Coefficient [m/(m·K)] | ≤2.2×10-4 | ||
Fire Resistance | UL 94-V1 |
(Pls note: the above data for this product in 25 °C temperature, 55 percent humidity conditions, for reference. The accurate data is measured by customers when using.
The appearance can be adjusted by our technical department if required.)
TECHNICAL GUIDELINES of Addition thermal conducted silicone HY- 9055
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Weight Ratio: part A: part B = 1:1
3, Deaeration the mixture under 0.08 MPa for 3 minutes.
4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.
Warm Tips:
1.The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.
lCondensation silicone which not completely cured or organic tin compounds
lSulphur, sulfide and sulfur rubber materials.
lAmine compounds as well as contains the amine materials.
lPewters solder flux.
2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.
3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix 9301 evenly before using, it does not affect the performance.
PACKAGE
20Kg/pail (Part A10Kg + Part B10Kg)
SHELF LIFE AND TRANSPORTATION
1. Twelve(12) months from date of shipment when stored at 24C in original unopened packages.
2. This kind of product is non-dangerous product, it can be transported as general chemicals.
3. Products exceed the storage life should be confirmed normal before using
Any more information please feel free to contact Maggie: