group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
model9055#9301#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:47:02 GMT
Certification SGS,MSDS,RoHS
HARDNESS 55+/-5
Mixing Ratio 1:1
Type htv silicone rubber
Appearance Fluid
Certificated RoHS, Reach, MSDS,SGS.ISO9001:2008
EINECS No 39100000
Purity 100%
Min Order200 kilogram
Usage of transparent electronic potting compound silicone rubber :
filling for LED,LCD electronic display,circuit board.
Description of transparent electronic potting compound silicone rubber :
hy210 is condensation silicone potting compound in two parts with low viscosity.it can be cured completely at room temprature,hy210 works on the surface of material as PC(poly-carbonate)PP,ABS,PVC as to its superior bonding feature.it is also applicable for insulation ,waterproof and bonding of electronics parts.it meets the requirements of european rohs.
Typical application of transparent electronic potting compound silicone rubber :
potting for protection of general electronic module.
ourdoor protection for LED screen.
Warm tips:
1.sealing pakage for storage,the mixture should be used up at once to avoid wasting.
2.silicone belongs to non-dangerous goods,but keep away form mouth and eyes.
3.when it gets stratified after a period of storage,please mix hy210 evenly before using.it does not affect the perfomance.
Package of transparent electronic potting compound silicone rubber :
22kg/sed(part A 20kg + part B 2kg)
shelf life and transportation:
1.twelve (12) months when stored at 24 degree celsius in original unopened packages.
2.this kind of product is non-dangerous product,it can be transported as general chemicals.
3.products exceed the storage life should be confirmed normal before using.
technical guidelines of transparent electronic potting compound silicone rubber :
1.pls put part A and part B in separate container and stir evenly before mixing the two-parts todether.
2.weight ratio/part A/part B=10:1
3.bubble release if necessary,deaeration the mixture under 0.08 mpa for 3 miutes.
4.hy210 is cured at room temperature,so pls put it under room temperature after pouring,it comes to next process when basically cured,and it takes about 24 hours for completely cured.
kindly note-----temperature and humidity with a tremendous influences for curing of hy210.
Technical parameters:
Properties index | Part A | Part B | |
Before Curing
| Appearence | Black fluid | Colorless/yellowish fluid |
Viscosisty(cps) | 2500±500 | - | |
Features when operation | Mixing Ratio(By weight) | 10/1 | |
Operating Time(25°C /min) | 20~30 | ||
Curing time(hr,basically cured) | 3 | ||
Curing time(hr,perfectly cured) | 24 | ||
Hardness(shore A) | 15±3 | ||
After Curing | Thermal Conductivity[W(m·K)] | ≥0.2 | |
Dielectric Strength(kV/mm) | ≥25 | ||
Dielectric permittivity(1.2MHz) | 3.0~3.3 | ||
Volume resistivity(Ω·cm) | ≥1.0×1016 | ||
Fire Resistance | 94-V1 |
(pls note:all data of this product above in 25 degree celsius with 55% humidity conditions,we do not guarantee a same data if testing under different conditions,or when data was regenerated.)
Need any help on silicone rubber, please feel free to contact Ms Kitty:
Tel:86-755-89948294
Mob:86-15989267535
E-mail: hysh(at)szrl(dot)net
Skype:kity-467707861
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.