group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY9301
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:49:01 GMT
color white
HS code 39100000
sample available
normal packing 25kg per drum
delivery within 3 days
shelf life one year
certificate ISO9001:2000 FDA SGA RoHS
MOQ 200kgs
features liquild
Payment Terms T/T,L/C
Min Order200 kilogram
Specifical of Electronic Compound Silicone Rubber With High Quality
RTV-2 Silicone is a newly insulating materialsilicon of silicon compounds.
It cures without heat, corrosion and just with little shrinkage.
It can be applied to the sealing and pouring of various electronic components, and then forming insulation system.
Features of Electronic Compound Silicone Rubber With High Quality
a.Room temperature vulcanize, and easy to operate;
b.Maintain flexibility at a wide temperature range, and excellent insulation performance;
c.Waterproofing, moisture-proof, mouldproof, dustproof, and fixed components;
d.Resistance to Chemical dielectric, anti-yellowing, resistance to climate ageing.
Typical Application of Electronic Compound Silicone Rubber With High Quality
bonded seal of electronic components,
power module and control module, which requires waterproof and insulation.
LED screen,
Wind Power Generator,
PCB substrate, etc.
Technical Parameters
Before Curing | Appearence | Black/Transparent Fluid |
Density(25°C g/ml) | 0.98±0.02 | |
Viscosisty(25°Ccps) | Part A 500±100:Part B:800±100 | |
Mixing Ratio | A:B=1:1(By weight) | |
Operating Time(25°C hr) | 5 | |
Curing time(80°C hr) | 0.5 | |
After Curing | Hardness(Shore A) | 0-40 |
Dielectric Strength(KV/mm) | 23 | |
Volume Resistance(Ω.Cm) | 1.0×10 15 | |
Permittivity(1.2MHz) | 3.0 | |
Temperature Resistence(°C) | -60~200 | |
Fire Resistance | UL94-V1 |
(Pls note: all data of this product above in 25 °C with 55% humidity conditions. We don’t guarantee a same data if testing under different conditions, or when data was regenerated)
TECHNICAL GUIDELINES
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Weight Ratio: part A: part B = 1:1
3, Deaeration the mixture under 0.08 MPa for 3 minutes.
4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.
Warm Tips:
1.The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.
l Condensation silicone which not completely cured or organic tin compounds
l Sulphur, sulfide and sulfur rubber materials.
l Amine compounds as well as contains the amine materials.
l Pewters solder flux.
2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.
3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix 9301 evenly before using, it does not affect the performance.
PACKAGE
20Kg/pail (Part A10Kg + Part B10Kg)
SHELF LIFE AND TRANSPORTATION
1. Twelve(12) months from date of shipment when stored at 24C in original unopened packages.
2. This kind of product is non-dangerous product, it can be transported as general chemicals.
3. Products exceed the storage life should be confirmed normal before using.
Our factory
Any questions about Electronic Compound Silicone Rubber With High Quality please feel free to contact Maggie