Addition thermal conducted liquid silicone rubber

FOB Price

US $10.98
200 - 40,000 kilogram
US $8.28
40,001 - 999,999 kilogram

group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY9055# silicone rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 19:49:54 GMT

contact supplier

Paramtents

payment T/T L/C Western Union
package 25kg/drum 200kg/drum
MOQ 200kg
Feature liquid
Sample avalible
Hardness 10~50shore A
color all color available
certificate SGS, MSDS, RoHS
HS Code 39100000

Packging & Delivery

Min Order200 kilogram

Briefing

Addition thermal conducted silicone rubber
favrable hardness
for electronic potting
good tensile
good tear strength

Detailed

Technical Parameters of Addition thermal conducted silicone rubber

Specification		Part A	Part B
Before Curing	Appearance	Dark Grey Fluid	White Fluid
	Viscosity(cps)	2500±500	2500±500
Operating Performance	Part A:Part (By weight)	1:1
	Viscosity after mixing (cps)	2000~3000
	Operating Time (min)	120
	Curing Time (min, 25°C)	480
	Curing Time (min, 80°C)	20
After Curing	Hardness (shore A)	55±5
	Heat Conductivity [W(m·K)]	≥0.8
	Dielectric Strength(kV/mm)	≥25
	Permittivity(1.2MHz)	3.0~3.3
	Volume Resistance(Ω·cm)	≥1.0×1016
	Linear Expansion Coefficient [m/(m·K)]	≤2.2×10-4
	Fire Resistance	UL 94-V1

Addition thermal conducted liquid silicone rubber

Typical Application of Addition thermal conducted silicone rubber

9055 is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.

Product Feature of Addition thermal conducted silicone rubber

It can be applied to the sealing and pouring of various electronic components, and then forming insulation system with no corrosion and negligible shrinkage.

Addition thermal conducted liquid silicone rubber

TECHNICAL GUIDELINES of Addition thermal conducted silicone rubber

1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.

2, Weight Ratio: part A: part B = 1:1

3, Deaeration the mixture under 0.08 MPa for 3 minutes.

4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.

Addition thermal conducted silicone rubber Warm Tips:
1.The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.

l Condensation silicone which not completely cured or organic tin compounds

l Sulphur, sulfide and sulfur rubber materials.

l Amine compounds as well as contains the amine materials.

l Pewters solder flux.

2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.

3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.

4. When it gets stratified after a period of storage, Please mix 9301 evenly before using, it does not affect the performance.

Addition thermal conducted silicone rubber PACKAGE
20Kg/pail (Part A10Kg + Part B10Kg)

Addition thermal conducted liquid silicone rubber