translucent liquid silicone rubber for shoe insole making description :
transparent silicone rubber for shoe insole making is generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.
translucent liquid silicone rubber for shoe insole making main application:
translucent liquid silicone rubber for shoe insole making main properties:
translucent liquid silicone rubber for shoe insole making
(The mixing ratio of part A and part B can be adjusted to 1:1or 10:1) (25°C)
Product | E-615 | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 15±2 | 20±2 | 25±2 | 30±2 | 42±2 |
Mix ratio(A:B) | 1:1 | 1:1 | 1:1 | 1:1 | 10:1 |
Viscocity Part A(mPa.s) | 22000±2000 | 23000±2000 | 27000±2000 | 25000±2000 | 55000±2000 |
Viscocity Part B(mPa.s) | 1900±500 | 1900±500 | 1800±500 | 2400±500 | 150±50 |
Tensile strength (MPa) | 5.2 | 5.7 | 6.7 | 5.5 | 7.6 |
Tear-strength (kN/m) | 25 | 26 | 23 | 24 | 22 |
Elongation(%) | 569 | 581 | 480 | 410 | 450 |
Density | 1.05 | 1.05 | 1.07 | 1.13 | 1.14 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 20-30mins(60°C) | 6-8hrs(25°C) 130-50mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
Notice:
All above addition silicone is forbidden to mix with organic compounds of condensation cure silicone rubber,otherwise, the silicone rubber will not cure, and also should not mix with organic compounds containing S, P, N as well as metallic salt of organic acids. It also will cause this product cure uncompletely or not cure.
Any questions of translucent liquid silicone rubber for shoe insole making, please feel free to contact Kaimi:
TEL: 086-755-89212369
FAX: 086-755-89948030
MOBILE:086-18938867528
Website: www(dot)szrl(dot)net
E-MAIL: hyju(at)szrl(dot)net
skype:hyjiangying
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.