group nameLiquid silicone rubber for insoles
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelQ625# silicone rubber
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 21:37:42 GMT
Hardness 25Shore A
MOQ 200kg
Payment T/T L/C Western union
Package 25kg/drum 200kg/drum
Features liquid
HS Code 39100000
Certifications RoHS, MSDS, SGS, ISO9001:2000
Min Order200 kilogram
Addition Platinum-Cure Silicone For Shoe Insole making main properties:
Addition Platinum-Cure Silicone For Shoe Insole Making Description :
Addition Platinum-Cure Silicone For Cake Molds are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage. The mixing ratio between Part A and Part B can be 10:1 or 1:1.
Addition Platinum-Cure Silicone For Shoe Insole making Main application:
Addition Platinum-Cure Silicone For shoe insole making(25°C)
(The mixing ratio of part A and part B can be adjusted to 1:1or 10:1)
Product | E-615 | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 15±2 | 20±2 | 25±2 | 30±2 | 42±2 |
Mix ratio(A:B) | 1:1 | 1:1 | 1:1 | 1:1 | 10:1 |
Viscocity Part A(mPa.s) | 22000±2000 | 23000±2000 | 27000±2000 | 25000±2000 | 55000±2000 |
Viscocity Part B(mPa.s) | 1900±500 | 1900±500 | 1800±500 | 2400±500 | 150±50 |
Tensile strength (MPa) | 5.2 | 5.7 | 6.7 | 5.5 | 7.6 |
Tear-strength (kN/m) | 25 | 26 | 23 | 24 | 22 |
Elongation(%) | 569 | 581 | 480 | 410 | 450 |
Density | 1.05 | 1.05 | 1.07 | 1.13 | 1.14 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 20-30mins(60°C) | 6-8hrs(25°C) 130-50mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
Notice:
All above addition silicone is forbidden to mix with organic compounds of condensation cure silicone rubber,otherwise, the silicone rubber will not cure, and also should not mix with organic compounds containing S, P, N as well as metallic salt of organic acids. It also will cause this product cure uncompletely or not cure.
Any more information about silicone rubber, pls feel free to contact Bella.
Mobile: 0086-18938867572
Tel: 0086-755-89948006
Fax: 0086-755-89948030
Website: www (dot) szrl (dot) net
Email:hysi(at)zrl(dot)net
Skype: bellajiaqi
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.