group nameinjection moulding silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE620 E625
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 21:47:34 GMT
color white/red/green/yellow
certificate RoHS.MSDS.SGS ISO9001:2000
Min Order200 kilogram
lace mold&cake design&casting&fine plaster&artstone sculpture& gold jewellery addition silicone rubber details
Delivery Time: within 3 days after payment confirmed in our bank.
Payment Terms: L/C,T/T
addition silicone rubber
Description
addition silicone rubberis generally named two-components silicone
rubber, Part A and part B. It features an exceptional fluidity and good operability. The
mixing ratio is 1:1,mainly be suitable for making molds application.
Applications
addition silicone rubbercould be mainly used for making concrete
stones, wax molds, PU molds, resin molds, gypsum casting, candle molding and
chocolate , candy and any other FDA food product mold making,prototyping etc.
Instruction of addition silicone rubber
addition silicone rubber are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2-3% curing agent, they can still be operated within 30 minutes, but will be formed after 2-3 hours. With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.
Features of Flexible addition silicone rubber
(1)high tensile & tear strength
(2) Low linear shrinkage
(3)free Curing agent
(4)brushing & pouring
(5) high duplication times
Technique Data Sheet of HY-E series addition silicone rubber
Product | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 20±2 | 25±2 | 30±2 | 42±2 |
Mix ratio(A:B) | 1:1/10:1 | 1:1/10:1 | 1:1/10:1 | 1:1/10:1 |
Viscocity Part A(mPa.s) | 23000±2000 | 27000±2000 | 25000±2000 | 30000±2000 |
Viscocity Part B(mPa.s) | 3500±500 | 3500±500 | 2400±500 | 6000±500 |
Tensile strength (kgf/cm2) | 45±5 | 48±5 | 50±5 | 65±5 |
Tear-strength (kN/m) | 20±2 | 22±2 | 18±2 | 16±2 |
Elongation(%) | 500±50 | 500±50 | 450±50 | 450±50 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 110-20mins(60°C) | 3-4hrs(25°C) 110-20mins(60°C) | 3-4hrs(25°C) 110-20mins(60°C) | 3-4hrs(25°C) 1 110-20mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 |
(Note: Other hardness is adjustable)
Any further information required of lace mold/cake design/casting/fine plaster/artstonesculpture/gold jewellery/ addition silicone rubber , pls feel free to contact Ms Kaimi
Mobile: 0086-18938867528
Tel: 0086-755-89212369
Fax: 0086-755-89948030
E-mail: hyju(at)szrl(dot)net
Website: www(dot)szrl(dot)net
skype:hyjiangying
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.