liquid trademark silicon rubber for T-shirt

FOB Price

US $11.30
200 - 40,000 kilogram
US $7.80
40,001 - 999,999 kilogram

group namesilicone rubber for textile coating& trademarks
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelHY-966,HY-967
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 21:58:15 GMT

contact supplier

Paramtents

color adjustable
certificate ISO9001:2000,SGS,RoHS
application for apparel,T-shirt
delivery within 3 days after paymnet
MOQ 200 kg
payment terms T/T, L/C
transportation by sea
shelf life 12 months
packing vaccum pumping

Packging & Delivery

Min Order200 kilogram

Briefing

high transparency
waterproof
moderate viscosity
high temperature resistance

Detailed

liquid trademark silicon rubber for T-shirt

The series of trademark silicon rubberis divided into dispensing type HY-966 and coating type HY-967. They can not only be fabricated into trademarks independently, but also be fabricated into trademarks through cloth pressing and leather pressing.

HY-966A/HY-966B dispensing type trademark silicone rubber belongs to liquid addition cure system. The amount of the curing agent can be 10% and can also be adjusted to the mixing proportion of 1 : 1. The curing agent is two-component high-strength liquid silicone rubber made of basic compound, cross-linking agent, catalyst, padding and additive. Those materials do not contain heavy metal and aroma solvent, hence, it's not harmful to human body.

liquid trademark silicon rubber for T-shirt Datasheet:

Item no.	HY-966		HY-967
Component	A	B	A	B
Appearance	Transparent	Transparent	Transparent	Transparent
Mix ratio (%)	10	1	10	1
Viscosity (cps)	≥40000		≥35000
Pot life (H)	1-1.5		1-1.5
Curing time (H)	12-16		12-16
Elongation (%)	≥400		≥400
Tear strength (KN/m)	≥15		≥20
Hardness (A°)	Hardness can be adjusted according to the requirements of customers (20-28 A°)

Typical curing Condition of liquid trademark silicon rubber for T-shirt :170°C×5mins, prolong or shorten the curing time appropriately according to the thickness and size of the product during actual use.

liquid trademark silicon rubber for T-shirt

Silicone rubber for trademark Using Instructions: The mixing proportion of HY-966A and HY-966B is 10:1. Mix component A and component B sufficiently and evenly according to the mixing proportion before use. The process of vacuum-pumping is also needed.

Note: The series of products must not be in contact with organisms like N, P, S, etc., ionic compounds like Hg, Bi, As, etc., and alkynes, vinyl compounds, etc. to avoid the situation at the products can not be cured due to platinum catalyst poisoning. The products particularly can not be in contact with PVC which contains lead causing catalyst poisoning. Some organic pigment also can slow down the curing time or cause uncured .
After HY-966A and HY-966B are mixed, the silicone rubber must be used up within 4 hours, otherwise the cross-linking and curing arises to lose effectiveness. In case of a higher surrounding temperature, more attention should be paid.

liquid trademark silicon rubber for T-shirt

Instruction of liquid trademark silicon rubber for T-shirt: Typical data can not be directly used for actual production guidance. Please contact us for details.

Package of : liquid trademark silicon rubber for T-shirt:General packages of HY-966 and HY-967 products is in 5kg per can, 20kg per pail and 200kg per barrel.

Precautions of liquid trademark silicon rubber for T-shirt: The products can be transported as safety and non-hazardous goods since they are noninflammable with resistance to a high temperature above 300°C.

For more information about the liquid trademark silicon rubber for T-shirt , pls contact with miss Caroline at any time

TEL: +86-755-89948019

Mobile: +86-18938867567

Skype: cathy19900719

Email: hysf(at)szrl(dot)net

Website : www(dot)szrl(dot)net