group namesilicone rubber for textile coating& trademarks
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelSB4130,SB4140
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 22:00:48 GMT
color adjustable
certificate ISO9001:2000,SGS,RoHS
application for apparel,T-shirt
delivery within 3 days after paymnet
MOQ 200 kg
payment terms T/T, L/C
transportation by sea
shelf life 12 months
packing vaccum pumping
Min Order200 kilogram
liquid silicon rubber for trademarks
The series of liquid silicon rubber for trademarks is divided into dispensing type HY-966 and coating type HY-967. They can not only be fabricated into trademarks independently, but also be fabricated into trademarks through cloth pressing and leather pressing.
HY-966A/HY-966B dispensing type trademark silicone rubber belongs to liquid addition cure system. The amount of the curing agent can be 10% and can also be adjusted to the mixing proportion of 1 : 1. The curing agent is two-component high-strength liquid silicone rubber made of basic compound, cross-linking agent, catalyst, padding and additive. Those materials do not contain heavy metal and aroma solvent, hence, it's not harmful to human body.
liquid silicon rubber for trademarks Datasheet:
Model | SB4130 | SB4140 |
Appearance | Transparent | Tranparent |
Hardness(shore A) | 30±2 | 40±2 |
Mix ratio(A:B) | 01:01 | 01:01 |
Viscosity(mPa.s) | 65000±2000 | 67000±2000 |
Tensile strength(Mpa) | 4.2 | 4.1 |
Tear-strength(KN/m) | 17±2 | 17±2 |
Elongation(%) | 275 | 270 |
Pot life/working time(25°C) | 6-24hrs | 6-24hrs |
curing time(100-120°C) | 3-10(minutes) | 3-10(minutes) |
Typical curing Condition of liquid silicon rubber for trademarks:
170°C×5mins, prolong or shorten the curing time appropriately according to the thickness and size of the product during actual use.
liquid silicon rubber for trademarks Using Instructions:
The mixing proportion of HY-966A and HY-966B is 10:1. Mix component A and component B sufficiently and evenly according to the mixing proportion before use. The process of vacuum-pumping is also needed.
Note: The series of products must not be in contact with organisms like N, P, S, etc., ionic compounds like Hg, Bi, As, etc., and alkynes, vinyl compounds, etc. to avoid the situation at the products can not be cured due to platinum catalyst poisoning. The products particularly can not be in contact with PVC which contains lead causing catalyst poisoning. Some organic pigment also can slow down the curing time or cause uncured .
After HY-966A and HY-966B are mixed, the silicone rubber must be used up within 4 hours, otherwise the cross-linking and curing arises to lose effectiveness. In case of a higher surrounding temperature, more attention should be paid.
Instruction of liquid silicon rubber for trademarks:
Typical data can not be directly used for actual production guidance. Please contact us for details.
Package of liquid silicon rubber for trademarks:
General packages of HY-966 and HY-967 products is in 5kg per can, 20kg per pail and 200kg per barrel.
Precautions of liquid silicon rubber for trademarks:
The products can be transported as safety and non-hazardous goods since they are noninflammable with resistance to a high temperature above 300°C.
For more information about the liquid silicon rubber for trademarks, pls contact with miss Caroline at any time
TEL: +86-755-89948019
Mobile: +86-18938867567
Skype: cathy19900719
Email: hysf(at)szrl(dot)net
Website : www(dot)szrl(dot)net
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.