group nameAddition cure silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE630 silicone
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 22:01:22 GMT
Sample Free
Shelf Life 18 months
Certificate ISO9001:2000,FDA,RoHS
Operating time (hour 25 0C ) 0.5
Colour Any
Hardness(shore A) 15-42
Mix Ratio 1;1
Elongation-break(%) 320-520
Curing time(hour) 3-5
Dynamic Viscosity (mPa.s) 8000-14000
Min Order200 kilogram
Addition cure concrete mold silicone with different hardness
1.Description of Addition cure concrete mold silicone with different hardness
Addition cure silicone molds for concrete are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage.
The mixing ratio between Part A and Part B can be 10:1 or 1:1.
2.Main application of Addition cure concrete mold silicone with different hardness
· GRC and Concrete moulding
· PU resin casting
· General Mouldmaking
· Superior manual mold design
3.Main properties of Addition cure concrete mold silicone with different hardness
· almost nil shrinkage
· high chemical resistance to aggressive components of some types of resins
· good tear strength (this feature ensures higher resistance to wearing and shearing)
· high degree of precision in reproduction
· high dimensional stability over time and non-deformability
· high resistance to high temperatures and ageing (resit to -60-200°C)
· excellent non-stick effect
· environmental, odorless and nontoxic
4. Addition cure concrete mold silicone with different hardness datasheet (25°C)
Product | E-615 | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 15±2 | 20±2 | 25±2 | 30±2 | 40±2 |
Mix ratio(A:B) | 1:1 | 1:1 | 1:1 | 1:1or 10:1 | 1:1or10:1 |
Viscocity Part A(mPa.s) | 9000±2000 | 11000±2000 | 15000±2000 | 20000±2000 | 55000±2000 |
Viscocity Part B(mPa.s) | 1900±500 | 1900±500 | 1800±500 | 2400±500 | 150±50 |
Tensile strength (MPa) | 6.2 | 6.5 | 6.7 | 7.2 | 7.6 |
Tear-strength (kN/m) | 25 | 26 | 23 | 24 | 22 |
Elongation(%) | 569 | 581 | 480 | 440 | 450 |
Density | 1.05 | 1.05 | 1.07 | 1.13 | 1.14 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 20-30mins(60°C) | 6-8hrs(25°C) 30-50mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
5.Package of Addition cure concrete mold silicone with different hardness
6.Certificationsof Addition cure concrete mold silicone with different hardness
7.Our factory:
Any questions, please feel free to contact Mr Lucas:
TEL: 086-755-89212369
FAX: 086-755-89948030
MOBILE:086-18898736056
E-mail: hysj(at)szrl(dot)net
You can also send me E-mail by scanning QR Code below:
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.