fire and smoke curtains coating silicone rubber

FOB Price

US $12.56
200 - 40,000 kilogram
US $7.96
40,001 - 999,999 kilogram

group namesilicone rubber for textile coating& trademarks
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelTB3115
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 22:19:38 GMT

contact supplier

Paramtents

Available color Transparent
Certifications RoHS.MSDS.SGS ISO9001:2000
Hardness 15±2
Curing time 20 - 30min
Mixing proportion of curing agent 10:1
Operating time 12-24 hours
Viscosity (MPas -25 0C) 60000~100000
Tensile-strength(kgf /cm2 ) 4.6
Tear-strength(KN/m) 20±2

Packging & Delivery

Min Order200 kilogram

Briefing

fire and smoke curtains coating silicone rubber
Low shrinkage(<0.1%)
Good skid-proof effect
High temperature resistance
SGS

Detailed

Application of fire and smoke curtains coating silicone rubber:

Besides for fire and smoke curtains, it can be used for coating of fire blankets, fire shutter, firewall, insulating cloth and other fields for the manufacture of high temperature piping (such as non-metallic compensator, hot air channel), cut off the power, chemical, cement, iron and steel, petroleum etc.

The coationg silicone rubber also can be used for skid-proof purpose of frilals, underclothes and widely applied for cotton fabric, polyester-mixed cotton cloth, nylon cloth, flax, woolen, insulating cloth, etc.

fire and smoke curtains coating silicone rubber

Features of Silicone Ink for Printing or Coating on Textile:

-Low shrinkage(<0.1%)

-Good skid-proof effect and high adhesive strength

-Wearproof, wash-resistant, high temperature resistant

-Non-toxic and odorless, food grade silicone

-High transparency and good tear-strength.

fire and smoke curtains coating silicone rubber

Datasheet of Liquid Silicone Rubber For Coating Textiles:

Model	TB3115	TB3120
Appearance	Transparent	Transparent
Hardness(shore A)	15±2	20±2
Mix ratio(A:B)	10:1	10:1
Viscosity(mPa.s)	60000~100000	60000~100000
Tensile strength(Mpa)	4.6	4.8
Tear-strength(KN/m)	20±2	22±2
Elongation(%)	450	450
Pot life/working time(25°C)	12-24 hours	12-24 hours
curing time(125°C)	30~50 seconds	30~50 seconds