100 - 40,000 kilogram
40,001 - 999,999 kilogram
group namePad printing silicone rubber
Min Order100 kilogram
brand nameHong Ye silicone rubber
model918#,900#,911#,912#,2018#,268#
payment methodT/T, L/C, Westem Union
update timeFri, 08 Nov 2013 22:56:34 GMT
Certification IS 9000,SGS, RoHS, MSDS
Color white,yellow,red,blue
Hardness 10-42A
Purity 100%
Application pad printing materials
Sample Free
Technical support Free
Transportation By sea or by air
EINECS No 39100000
Mixing ratio 3%-5%
Min Order100 kilogram
Manufacture of silicone rubber for making pads
( with certificate of MSDS,SGS,RoHS)
Pad printing silicone application:
Silicone rubber,pad printing silicone rubber is mainly used for printing irregular patterns of plastic toys, electroplating products, electronic toys, trademarks. Silicon pad is a carrier which transfer printing the patterns on the steel plate onto the toy products' surface.
Pad printing silicone rubber features:
Pad printing silicone rubber with high print times and abrasion resistance, good printing effect, permanent and durable, all kinds of colors are available and our catalyst is free charged.
Pad printing silicone rubber operation instructions:
Pad printing silicone rubber is two-component silicone, part A is the liquid silicone rubber, part B is the catalyst. The usual mxing ratio for silicone rubber and catalyst is 100 : 2-3, eg. we take 100grams of liquid silicone rubber,then we add 2-3 grams catalyst, mix then evenly and pour it to your mold. Then after 2-4 hours, you will obtain a printing pad.
Admixture amount of curing agent and silicon rubber reactions:
5.1Added with 1% of curing agent,silicon can still flow within 2.5 hours,mold can be released in 6-8 hours.
5.2Added with 2% of curing agent,silicon can still flow within 50 minutes to 1 hour,mold can be released in 2-3 hour
5.3Added with 3% of curing agent,silicon can still flow within 28-30 minutes,mold can be released in 1.5-2 hours.
5.4Added with 4% of curning agent,silicon can still flow within 10-15 minutes,mold can be released in 1-1.5 hours.
5.5 Curing agent reaction rate is related with weather and temperature. Under 25 degree,they can be added according to the instruction or at double amount in winter or under subzero temperature.
(Note: curing agent can not be added above the 4 maximum level and the normal proportion is 2.If more than 4 is applied,the silicon will condensate too fast for normal usage).Above is the mixing data for silicon and curing agent,the precise result of hundreds of times of our experiments. Provided that you arrange production according to our instruction,you are sure to manufacture first class products and maximize your profitthis is not only the need of,but also our responsiblity for and a satisfactory answer to our customers.
Frequently asked questions of pad printing silicon rubber ?
Why does the silicone pad can not drop oil well?
During the process of manufacturing toys, the steel mold need to spray the release agent for every dozens of products, the first or second product exists lots of release agent on the surface regarding the mold having just sprayed with the release agent. It is very normal that the incomplete printing patterns of more than 2 in 10 plastic toys or products which are not sprayed with paint may not drop ink well. If the product is directly taken for pad printing before being cleaned by the thinner, hence, the phenomenon just arises.
Any further information required ,pls feel free to contact Miss Berryand call the mobile of 0086-18938867580or the phone 0086-755-89212365. Welcome to visit www(dot)szrl(dot)netanytime .