group nameelectronic potting silicone rubber
Min Order200 kilogram
brand nameHong Ye silicone rubber
model9055
payment methodT/T, L/C, Westem Union
update timeSat, 09 Nov 2013 12:33:47 GMT
Color white/grey
Min Order200 kilogram
Electronic Potting two Compound silicone Feature
HY 9055 is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate),PP,ABS,PVC, etc. and metal materials.
Electronic Potting two Compound silicone Typical Application
HY 9055 could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
Features | Part A | Part B | |
Before Curing | Appearence | Gray Fluid | White Fluid |
Viscosisty(25°Ccps) | 2500±500 | 2500±500 | |
Operation features | Mixing Ratio | 1:1 | |
Viscosisty(after mixing) (cps) | 2000~3000 | ||
Operating Time(25°C hr) | 120 | ||
Curing time (min,25°C) | 480 | ||
Curing time(80°C hr) | 20 | ||
After Curing | Hardness(Shore A) | 55±5 | |
Thermal conductivity [W(m·K)] | ≥0.8 | ||
Dielectric Strength(KV/mm) | ≥25 | ||
Permittivity(1.2MHz) | 3.0~3.3 | ||
Volume Resisivity(Ω·cm) | ≥1.0×1016 | ||
linear expansibility [m/(m·K)] | ≤2.2×10-4 | ||
Fire Resistance | 94-V1 |
Electronic Potting two Compound silicone TECHNICAL GUIDELINES
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Mixing Ratio: part A: part B = 1:1
3, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4, Pls note that the thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80~100°C, the silicone will cure in 15 minutes; while in 25°C room temperature, the silicone will cure around 8 hours.
For get further information about our silicone product, PLS contact with Miss Rose:
Tel: 0086-755-89948294
Fax: 0086-755-89948030
Mobil: 0086-18938867525
E-mail: hyjz(at)szrl(dot)net
MSN: ross1024(at)msn(dot)cn
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.