group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelE630 silicone
payment methodT/T, L/C, Westem Union
update timeSat, 09 Nov 2013 12:36:39 GMT
Sample Free
Shelf Life 18 months
Certificate ISO9001:2000,FDA,RoHS
Operating time (hour 25 0C ) 0.5
Colour Any
Hardness(shore A) 15-42
Mix Ratio 1;1
Elongation-break(%) 320-520
Curing time(hour) 3-5
Dynamic Viscosity (mPa.s) 8000-14000
Min Order200 kilogram
Liquid silicone for concrete molds (platinum cure)
1.Description of Liquid silicone for concrete molds (platinum cure):
Liquid silicone for concrete molds(platinum cure) are generally named as two-part addition silicone rubber that vulcanises at room temperature.Part A is a flowable liquid, part B is the curing agent(platinum catalyst). It features an exceptional fluidity ,good operability,excellent physical properties and very low shrinkage.
The mixing ratio between Part A and Part B can be 10:1 or 1:1.
2.Main application of Liquid silicone for concrete molds(platinum cure):
· GRC and Concrete moulding
· PU resin casting
· General Mould making
· Superior manual mold design
3.Main properties of Liquid silicone for concrete molds(platinum cure):
· almost nil shrinkage
· high chemical resistance to aggressive components of some types of resins
· good tear strength (this feature ensures higher resistance to wearing and shearing)
· high degree of precision in reproduction
· high dimensional stability over time and non-deformability
· high resistance to high temperatures and ageing (resit to -60-200°C)
· excellent non-stick effect
· environmental, odorless and nontoxic
4.Liquid silicone for concrete molds (platinum cure) standard datasheet (25°C)
Product | E-615 | E-620 | E-625 | E-630 | E-642 |
Appearance | Translucent | Translucent | Translucent | Translucent | Translucent |
Hardness(shore A) | 15±2 | 20±2 | 25±2 | 30±2 | 40±2 |
Mix ratio(A:B) | 1:1 | 1:1 | 1:1 | 1:1or 10:1 | 1:1or10:1 |
Viscocity Part A(mPa.s) | 9000±2000 | 11000±2000 | 15000±2000 | 20000±2000 | 55000±2000 |
Viscocity Part B(mPa.s) | 1900±500 | 1900±500 | 1800±500 | 2400±500 | 150±50 |
Tensile strength (MPa) | 6.2 | 6.5 | 6.7 | 7.2 | 7.6 |
Tear-strength (kN/m) | 25 | 26 | 23 | 24 | 22 |
Elongation(%) | 569 | 581 | 480 | 440 | 450 |
Density | 1.05 | 1.05 | 1.07 | 1.13 | 1.14 |
Pot life/working time (mins) | 30-40 | 30-40 | 30-40 | 30-40 | 30-40 |
Curing time/setting time (hrs) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 120-30mins(60°C) | 3-4hrs(25°C) 20-30mins(60°C) | 6-8hrs(25°C) 30-50mins(60°C) |
Shrinkage rate (%) | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 |
5.Package of Liquid silicone for concrete molds (platinum cure):
6.Certificationsof Liquid silicone for concrete molds(platinum cure):
7.Company profile:
Shenzhen Hong Ye Jie Technology Co., Ltd, which was established in 1998, is a
Science and technology corporation which is engaged in production, R & D, and
sales of silicone rubber.
Our staff of sales and technical support is available to help you in selecting the right silicone rubber for your application as well as to provide you with samples of our products for evaluation. At Hong Ye Jie, we are committed to providing the highest level of customer service, competitive pricing, speedy delivery and a comprehensive, cutting-edge product offering.
Our ultimate goal is your satisfaction.
Need the price or other information for reference,please help us confirm some question first
1) How about the size of your products?
2) Will you make the silicone mold by pouring way or brushing way ?
3) What's the raw material of your products ? Plaster? resin or other?
Then we will according it to recommend the most suitable RTV silicone with the best price for your reference.
Any questions, please feel free to contact Mr Lucas:
TEL: 086-755-89212369
FAX: 086-755-89948030
MOBILE:086-18898736056
E-mail: hysj(at)szrl(dot)net
You can also send me E-mail by scanning QR Code below:
网络文化经营许可证:浙ICP备14006100号-11 2007-2024 Tradevv.com. All rights reserved.