liquid silicone rubber for concrete baluster mold

FOB Price

US $8.25
200 - 40,000 kilogram
US $6.20
40,001 - 999,999 kilogram

group nameRTV-2 silicone rubber for molds making
Min Order200 kilogram
brand nameHong Ye silicone rubber
modelmolding silicone rubber
payment methodT/T, L/C, Westem Union
update timeSat, 09 Nov 2013 12:38:08 GMT

contact supplier

Paramtents

Sample Free
Certification: SGS,MSDS,RoHS
Hardness: 25-40 shore A
Mixing Ratio: 2-3%
Shelf life 12 month
Operating time (hour 25 0C ) 0.5
Elongation-break(%) 180-450
EINECS No: 39100000
Curing time(hour) 3-5
Curing agent: 3%for free charged

Packging & Delivery

Min Order200 kilogram

Briefing

1. Resistance to deformation, high-temperature
2. High reproduction times
3. Good tensile strength
4. Exceptional fluidity

Detailed

liquid silicone rubber for concrete baluster mold

1. Application for liquid silicone rubber for concrete baluster mold

Liquid Silicone Rubber for concrete baluster mold is primarily intended for poly resin crafts, PU crafts, PU resin crafts, gypsum crafts, unsaturated resin crafts, lighting and candles crafts, plastic toy, stationery gifts crafts industry, a large statue Buddha, relievo furniture, furniture decorative materials, statues Buddha, artifacts copied, building decoration materials, large-scale cement mold, artificial fossils Factory, Europe component factory, simulation landscapes, animals and plants sculpture, sandstone crafts and so on.

liquid silicone rubber for concrete baluster mold

2. Instruction for liquid silicone rubber for concrete baluster mold

Add curing agent of 2%-3% at the room temperature, the silicone rubber is still operational within 30 minutes, and in 2-3 hours.

1. Adding curing agent 1%, the silicone rubber can still be operated within 2.5 hours and can be Demoulded after 6-8 hours.

2. Adding curing agent 2%, the silicone rubber can still be operated within 50 minutes to 1 hour and can Be demoulded after 2-3 hours.

3. Adding curing agent 3%, the silicone rubber can still be operated within 28 - 30 minutes and can bedemoulded after 1.5-2 hours.

4. Adding curing agent 4%, the silicone rubber can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.

liquid silicone rubber for concrete baluster mold

3.Standand datasheet of liquid silicone rubber for concrete baluster mold

Model	Color	Mixing ratio (%)	Operation Time (mins)	Demould	Hardness ( A0 )	Tensile-strength (MPa)	Tear-strength (kN/m)	Dynamic Viscosity	Shrinkage	Elongation
				time				(mPa.s)	rate (%)	(%)
				( hrs)
625#	white/translucent	100;3	30-40	3 to 4	25±2	3.4	24±2	25000±2000	≤0.3	410
630#	white/translucent	100;3	30-40	3 to 4	30±2	4	26±2	27000±2000	≤0.3	420
638#	white/translucent	100;3	30-40	3 to 4	38±2	4	25±2	25000±2000	≤0.3	450
640#	white/translucent	100;3	30-50	4 to 5	40±2	3.5	21±2	15000±2000	≤0.3	180

liquid silicone rubber for concrete baluster mold

4.Operation Steps of liquid silicone rubber for concrete baluster mold

Step One: Take 100g of part A and add 2g of part B and mix the silicone rubber and curing agent evenly.

Notes: Moulding silicon rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of white flowing liquid and part B is the curing agent.

Step Two: vacuum pumping

Without exception, this step takes less than 10 minutes.

Note: The time for vacuum-pumping should be less than 3—5 mins , otherwise, once the silicone rubber has cross-link reaction during vacuumizing, it will not be operated.

Step Three: Brushing cast & Perfusion Molding operation